THE MICROSTRUCTURE OF MANUAL ARGON ARC WELDING JOINT OF T91 STEEL TUBE
摘 要
对 60.3mm×8mm的T91钢管的母材及手工氩弧焊接头进行了化学成分、力学性能和显微组织的测定。结果表明,T91钢管的化学成分、力学性能和显微组织均满足GB 5310-1995的要求,焊接接头的组织为正常组织。
化学成分
力学性能
显微组织
T91 steel
Chemical composition
Mechanical property
Microstructure
Abstract
The chemical composition analysis, mechanical properties testing and microstructure analysis of the base metal and manual argon arc welding joint of T91 steel tube with size of 60.3mm×8mm have been done in the paper. The results show that the chemical composition, mechanical properties and microstructure of T91 steel tube with size of 60.3mm×8mm meet the requirement of standard GB 5310-1995, and the microstructure of joint shows normal.
中图分类号 TG142.73
所属栏目
基金项目
收稿日期 2005/1/12
修改稿日期
网络出版日期
作者单位点击查看
备注龚正春(1962-),男,高级工程师,学士。
引用该论文: GONG Zheng-chun,TANG Xin-ping,MENG Ling-qing,YOU Gong. THE MICROSTRUCTURE OF MANUAL ARGON ARC WELDING JOINT OF T91 STEEL TUBE[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2006, 42(11): 547～550
龚正春,唐信萍,孟令庆,犹公. T91钢管手工氩弧焊接头的显微组织[J]. 理化检验－物理分册, 2006, 42(11): 547～550
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】李春光,张晓东.SA213-T91钢小径管背面保护钨极氩弧焊接工艺[J］.吉林电力, 2001,(3):42.
【2】彭孙鸿,尤凤志,姜明娟,等.热穿孔温度对T91钢管持久强度的影响[J］.特殊钢, 2001,22(2):11-12.
【3】John Hald. Metallurgy and creep properties of new 9%~12%Cr steels[J］. Materials Technology, 1996,67(9):370-373.
【2】彭孙鸿,尤凤志,姜明娟,等.热穿孔温度对T91钢管持久强度的影响[J］.特殊钢, 2001,22(2):11-12.
【3】John Hald. Metallurgy and creep properties of new 9%~12%Cr steels[J］. Materials Technology, 1996,67(9):370-373.
相关信息