钢板表面发裂缺陷成因的初步探讨
THE TENTATIVE DISCUSSION ABOUT THE HAIRLINE CRACK DEFECTS OF STEEL PLATE
摘 要
热轧钢板和镀锌板多次出现表面发裂缺陷，利用光学金相和扫描电镜分析方法，对发裂缺陷的宏、微观形貌特征、缺陷部位钢的冶金质量变化等进行了检验和分析。认为,发裂缺陷是板坯连铸时产生的较深沟形振痕残余造成的。
缺陷
热轧钢板
镀锌板
振痕
Hairline crack
Defect
Hot rolling plate
Galvanized steel sheet
Vibration mark
Abstract
The hairline crack defects of hot rolling plate and galvanized steel sheet made in Benxi Iron &Steel (Group) Co. Ltd is studied through microscope and SEM in this paper. The metal graphic tests about the marostructure and microstructure of defects. The defects position and the changing of metallurgical quality are made in this paper. Basing on the above tests, we think that the hairline crack is induced by the remained deep vibration mark of casting slab.
中图分类号 TB303
所属栏目
基金项目
收稿日期 2006/4/28
修改稿日期
网络出版日期
作者单位点击查看
备注吕忠萍(1964)，女，高级工程师，学士。
引用该论文: LV Zhong-ping,XU Zhi-qiang. THE TENTATIVE DISCUSSION ABOUT THE HAIRLINE CRACK DEFECTS OF STEEL PLATE[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2006, 42(11): 551～553
吕忠萍,徐志强. 钢板表面发裂缺陷成因的初步探讨[J]. 理化检验－物理分册, 2006, 42(11): 551～553
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】上海金属学会编.金属材料缺陷金相图谱[M］.北京:机械工业出版社, 1981.
【2】德国钢铁学会.热轧、冷轧、热镀锌板带的表面缺陷图谱[M］.北京:中国金属学会钢铁编辑部, 2000.
【3】卢盛意.连铸坯质量[M］.北京:冶金工业出版社, 1994.
【4】卢盛意.连铸坯质量(第二版)[M］.北京:冶金工业出版社, 2000.
【2】德国钢铁学会.热轧、冷轧、热镀锌板带的表面缺陷图谱[M］.北京:中国金属学会钢铁编辑部, 2000.
【3】卢盛意.连铸坯质量[M］.北京:冶金工业出版社, 1994.
【4】卢盛意.连铸坯质量(第二版)[M］.北京:冶金工业出版社, 2000.
相关信息