双相不锈钢高温组织相含量的测定
MEASURING THE PHASE CONTENT OF HIGH TEMPERATURE MICROSTRUCTURE IN DUPLEX STAINLESS STEEL
摘 要
采用共聚焦激光扫描显微镜原位分析和淬火热处理试验两种方法并结合Mivnt显微图像分析系统对双相不锈钢高温组织中的奥氏体相含量(体积分数,下同)进行了测定。两种方法所测定的奥氏体相含量随温度的变化趋势基本一致。与热处理试验方法相比，共聚焦激光扫描显微镜原位分析方法的效率较高、测量结果较精确。根据两种分析方法测定的结果，得出了奥氏体相含量与温度的线性回归关系式。
共聚焦激光扫描显微镜
相含量
高温组织
Duplex stainless steel
Confocal scanning laser microscope
Phase content
High temperature microstructure
Abstract
The volume fraction of austenite in high temperature microstructure of duplex stainless steel was measured respectively by the confocal scanning laser microscopy (CSLM) in-situ analysis and solution quenching heat treatment test combined with Mivnt micrograph analysis system in this paper. The results of both methods are generally consistent. Compared to the method of heat treatment, the efficiency and measuring precision of the CSLM in-situ analysis are better. On the basis of the results of the CSLM in-situ analysis and quenching heat treatment test, the linear regress formula between the austenitic volume fraction and temperature is given.
中图分类号 TG113.12
所属栏目
基金项目 宝钢集团有限公司重点科研项目“超级双相不锈钢的关键技术研究”(BG050004)
收稿日期 2006/3/31
修改稿日期
网络出版日期
作者单位点击查看
备注周磊磊(1983-)，男，硕士研究生。
引用该论文: ZHOU Lei-lei,ZHOU Can-dong,LIN Gang,WANG Cheng-quan,LIN Da-wei,SONG Hong-wei. MEASURING THE PHASE CONTENT OF HIGH TEMPERATURE MICROSTRUCTURE IN DUPLEX STAINLESS STEEL[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2006, 42(11): 554～557
周磊磊,周灿栋,林刚,王成全,林大为,宋洪伟. 双相不锈钢高温组织相含量的测定[J]. 理化检验－物理分册, 2006, 42(11): 554～557
被引情况:
【1】刘丽,乙继海,刘贺,乔坚,张复懿, "三维激光共聚焦显微镜在复合轧辊组织研究中的应用",理化检验－物理分册 48, 446-449(2012)
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】Iza-mendia A, Pinol-juea A, Urcola J J, et al. Microstructural and mechanical behavior of a duplex stainless steel under hot working conditions[J］. Metallurgical and Materials Transactions, 1998,(29A):2975-2985.
【2】Yasuhiro, Maehara. Superplastic deformation mechanism of δ/γ duplex stainless steels[J］. Transaction ISIJ, 1987,(27):705-712.
【3】Hutchinson W H, Ushioda K, Runnsj G. Anisotropy of tensile behavior in a duplex stainless steel sheet[J］. Materials Science and Technology , 1985,(1):728-731.
【4】Wolfgang Reick, Michacl Pohl. Recrystallization-transformation combined reactions during annealing of a cold rolled ferritic-austenitic duplex stainless steel[J］. ISIJ international, 1998,38(6):567-571.
【5】刘持森.双相不锈钢中相含量的精确测定[J］.理化检验-物理分册, 2003,39(8):414-419.
【6】李尚周.双相不锈钢焊缝铁素体测定及影响因素分析[J］.华南理工大学学报, 1995,23(5):66-70.
【7】陈世修.奥氏体不锈钢中铁素体含量计算[J］.阀门, 2005,41(1):20-25.
【8】任永秀.奥氏体、铁素体-奥氏体双相不锈钢中α相含量测定方法对比试验[J］.理化检测-物理分册, 2005,41(4):184-194.
【9】毛萍莉.热处理对铸态双相不锈钢中δ-铁素体的影响[J］.沈阳工业大学学报, 2003,25(3):193-195.
【10】梁高飞,王成全,方 园,等.AISI304不锈钢加热过程中高温δ相形核与生长的原位观察[J］.金属学报, 2006,42(8):805-809.
【2】Yasuhiro, Maehara. Superplastic deformation mechanism of δ/γ duplex stainless steels[J］. Transaction ISIJ, 1987,(27):705-712.
【3】Hutchinson W H, Ushioda K, Runnsj G. Anisotropy of tensile behavior in a duplex stainless steel sheet[J］. Materials Science and Technology , 1985,(1):728-731.
【4】Wolfgang Reick, Michacl Pohl. Recrystallization-transformation combined reactions during annealing of a cold rolled ferritic-austenitic duplex stainless steel[J］. ISIJ international, 1998,38(6):567-571.
【5】刘持森.双相不锈钢中相含量的精确测定[J］.理化检验-物理分册, 2003,39(8):414-419.
【6】李尚周.双相不锈钢焊缝铁素体测定及影响因素分析[J］.华南理工大学学报, 1995,23(5):66-70.
【7】陈世修.奥氏体不锈钢中铁素体含量计算[J］.阀门, 2005,41(1):20-25.
【8】任永秀.奥氏体、铁素体-奥氏体双相不锈钢中α相含量测定方法对比试验[J］.理化检测-物理分册, 2005,41(4):184-194.
【9】毛萍莉.热处理对铸态双相不锈钢中δ-铁素体的影响[J］.沈阳工业大学学报, 2003,25(3):193-195.
【10】梁高飞,王成全,方 园,等.AISI304不锈钢加热过程中高温δ相形核与生长的原位观察[J］.金属学报, 2006,42(8):805-809.
相关信息