FRACTURE ANALYSIS ON STAINLESS MESH
摘 要
采用化学成分分析、金相检验、扫描电镜及X射线能谱分析等方法,对不锈钢丝网断裂原因进行了分析。结果表明,应力腐蚀及点腐蚀是引起不锈钢丝网断裂的主要原因,腐蚀介质为临海潮湿大气中的氯离子。断裂丝网材质较差,其化学成分不符合相关技术条件,铬、镍含量偏低,锰含量偏高均使1Cr18Ni9钢抗腐蚀性能下降,其显微组织中出现的较多弥散碳化物颗粒及铁素体大大降低了网丝的抗应力腐蚀和点腐蚀的性能。
Abstract
In this paper, chemical composition analysis, metallography, SEM and EDS methods were used to analysis the fracture failure of stainless mesh, the result showed that the fracture is caused by stress corrosion and pitting corrosion. The corrosion medium is chloride ion which is full in the damp atmosphere near the sea. The materials quality of the fracture stainless mesh was poor and the mesh chemical composition doesn′t meet the relative technical requirements, the contents of Cr and Ni are lower, however, the content of Mn is higher. All of these cause the stainless mesh failure in resistant to corrosion. The microscopic struture appears that a lot of dispersion carbide particles and ferrite blocks which greatly reduce the stainless mesh′s ability to resist stress corrosion and pitting corrosion.
中图分类号 TG356.4+5
所属栏目
基金项目
收稿日期 2006/2/6
修改稿日期
网络出版日期
作者单位点击查看
备注李剑容(1970-),男,工程师。
引用该论文: LI Jian-rong,WU Xing-hua,SUN Li,YOU Ju. FRACTURE ANALYSIS ON STAINLESS MESH[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2006, 42(11): 574~576
李剑容,吴兴华,孙黎,游菊,陈德华,马春霞. 不锈钢丝网断裂原因分析[J]. 理化检验-物理分册, 2006, 42(11): 574~576
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】任颂赞,张静江.钢铁金相图谱[M].上海:上海科学技术文献出版社, 2003.6.
【2】张静江.不锈钢管应力腐蚀开裂失效分析[A].上海第三届全国失效分析会议论文集[C].上海:上海材料研究所出版, 1988.
【3】王 荣.不锈钢换热器板片泄漏原因分析[J].理化检验-物理分册, 2006,41(5):255-257.
【2】张静江.不锈钢管应力腐蚀开裂失效分析[A].上海第三届全国失效分析会议论文集[C].上海:上海材料研究所出版, 1988.
【3】王 荣.不锈钢换热器板片泄漏原因分析[J].理化检验-物理分册, 2006,41(5):255-257.
相关信息