RESEACH OF SURFACE DEFECT IN COPPER-CONTAINING HOT ROLLING STEEL PLATE
摘 要
探究了含铜(0.025~0.28% Cu)热轧钢板表面月牙状、疤块状缺陷与铜富集相之间的关系,对钢板缺陷样品和相应的铸坯样品进行了一系列检验分析和相关热处理试验。结果表明,这类缺陷属折叠型缺陷,与局部表面的元素富集无关。
Abstract
In order to find out the relation between the surface defects (such as moon form, scab form) and copper phase enrichment on copper-containing steel plate (0.025%~0.28% Cu), a series of tests and the relevant heat treatment have been carried out in this paper. The result shows that this kind of defect belongs to the folding defect, having nothing to do with partial superficial enrichment of element.
中图分类号 TB303
所属栏目
基金项目
收稿日期 2006/4/24
修改稿日期
网络出版日期
作者单位点击查看
备注李建华(1966-),男,高级工程师,博士研究生。
引用该论文: LI Jian-hua,CHEN Shi-hua,CHEN Fang-yu. RESEACH OF SURFACE DEFECT IN COPPER-CONTAINING HOT ROLLING STEEL PLATE[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2006, 42(12): 606~609
李建华,陈士华,陈方玉. 含铜热轧钢板表面缺陷的研究[J]. 理化检验-物理分册, 2006, 42(12): 606~609
被引情况:
【1】周学俊,黄峰,王晶晶,陈江风, "镍铜质量比和硅含量对海洋环境用耐候钢电化学腐蚀行为的影响",腐蚀与防护 37, 789-792(2016)
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】J W Menter. The Heterogeneity of Steel[J]. Journal of The Iron and Steel Institute, 1971,209(4):249-263.
【2】刘富有.残余元素的表面富集与晶界氧化[J].金属学报, 1978,14(3):310-315.
【3】任海鹏.含Cu低合金钢表面氧化及热脆[J].东北工学院学报, 1993,14(1):36-39.
【4】李新城.车辆用含铜热轧钢板生产工艺研究[J].汽车工程, 2004,26(3):359-362.
【5】钟远标.Cu、Ni对钢水质量和钢材性能的影响[J].冶金丛刊, 1999,(4):40-42.
【6】张丽君.低碳钢表面氧化过程中铜的富集[J].东北大学学报(自然科学版), 2001,22(2):232-234.
【2】刘富有.残余元素的表面富集与晶界氧化[J].金属学报, 1978,14(3):310-315.
【3】任海鹏.含Cu低合金钢表面氧化及热脆[J].东北工学院学报, 1993,14(1):36-39.
【4】李新城.车辆用含铜热轧钢板生产工艺研究[J].汽车工程, 2004,26(3):359-362.
【5】钟远标.Cu、Ni对钢水质量和钢材性能的影响[J].冶金丛刊, 1999,(4):40-42.
【6】张丽君.低碳钢表面氧化过程中铜的富集[J].东北大学学报(自然科学版), 2001,22(2):232-234.
相关信息