T3铜管的腐蚀及其分析
CORROSION OF T3 COPPER TUBE AND ITS ANALYSIS
摘 要
T3铜管衬套在冷挤压成型前的软化退火、酸洗后其表面产生严重腐蚀,造成整批产品报废。对该产品及其腐蚀产物进行了金相检验、化学分析等检验，综合各项检验结果并采用模拟试验的方法详细分析了产生铜腐蚀的原因和机理。试验证实，在潮湿条件下铜与氯化物、铁等金属氧化物接触时的化学和电化学腐蚀，退火加热使衬套产生了严重腐蚀。
定性分析
晶粒边界线
吸氧腐蚀
析氢腐蚀
随炉升温
电极电位代数值
The red brown become scab
Qualitative analysis
The grain′s boundary line
Absorb the oxygen corrosion
Deposition hydrogen to decay
Heat with the stove
Algebra value of electrode potential
Abstract
Before cold extrusion T3 copper tube surface appears serious corrosion after soften anneal and pickling, which cause the whole products rejected. The reason and mechanism of the surface corrosion of T3 copper tube were researched by using chemical composition analysis, metallographic examination. By synthesizing various testing results and using the simulation testing, the results showed that under wet condition, the copper contacted with chlorides and ion to cause chemical and electrochemical corrosion, and the heating for anneal made the copper tube corrosion seriously.
中图分类号 TG146.1+1, TG172
所属栏目
基金项目 王力光(1949-),男，高级工程师。
收稿日期 2006/6/27
修改稿日期
网络出版日期
作者单位点击查看
引用该论文: WANG Li-gung,WANG Xiao. CORROSION OF T3 COPPER TUBE AND ITS ANALYSIS[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2006, 42(12): 610～612
王力光,王潇. T3铜管的腐蚀及其分析[J]. 理化检验－物理分册, 2006, 42(12): 610～612
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】浙江大学著.普通化学[M].上海:人民教育出版社, 1978.
【2】НД托马晓夫著.金属腐蚀及其保护的理论[M].北京:中国工业出版社, 1964.
【3】GB /T 5231-2001,加工铜及铜合金化学成分[S].
【2】НД托马晓夫著.金属腐蚀及其保护的理论[M].北京:中国工业出版社, 1964.
【3】GB /T 5231-2001,加工铜及铜合金化学成分[S].
相关信息