304不锈钢在硝酸环境中的腐蚀电化学行为
Electrochemical Corrosion Behavior of AISI Type 304 Stainless Steel in Nitric Acid Media
摘 要
采用极化曲线和电化学阻抗谱研究了硝酸温度和含量对304不锈钢耐蚀性能的影响。结果表明, 在钝化电位下, 304不锈钢在硝酸溶液中的阻抗呈现容抗特征, 阻抗值达到104 Ω·cm2, 形成的钝化膜致密完整, 随着温度的升高, 阻抗值和相位角都减小, 局部腐蚀加剧。高温和高含量均会促进钝化膜的溶解, 进而加速304不锈钢在硝酸中的腐蚀。
硝酸
电化学阻抗
304 stainless steel (SS)
nitric acid
electrochemical impedance spectroscopy (EIS)
Abstract
The effect of temperature and concentration of HNO3 on the corrosion behavior of 304 stainless steel(SS) was studied by potentiodynamic polarization curves and electrochemical impedance spectroscopy (EIS). The results indicated that the electrochemical impedance spectroscopy (EIS) of 304 SS presented capacitance loop with impedance approaching to 104 Ω·cm2 at passive potential, indicating the formation of a compact passivation film. With the increase of temperature, the impedance and phase angle decreased, localized corrosion was accelerated severely. High temperatures and high concentrations will promote the dissolution of the passive film, thereby accelerating the corrosion of 304 SS in nitric acid.
中图分类号 TG174.2 DOI 10.11973/fsyfh-201510001
所属栏目 试验研究
基金项目 国家自然科学基金(51076007/E060203); 中央基础研究基金; 北京市与中央高校共建项目
收稿日期 2014/10/11
修改稿日期
网络出版日期
作者单位点击查看
备注王奎升(1955-), 教授, 博士生导师, 从事石油与化工机械的教学与研究,
引用该论文: XU Yi-hui,KONG Ling-zhen,LU Wei,XU Guang-yuan,WANG Kui-sheng. Electrochemical Corrosion Behavior of AISI Type 304 Stainless Steel in Nitric Acid Media[J]. Corrosion & Protection, 2015, 36(10): 905
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】王玮, 罗明, 张启富. 沸腾稀硝酸中Cr6+对高纯不锈钢耐蚀性的影响[J]. 钢铁研究学报, 2009, 21(1): 47-50.
【2】NINGSHEN S, KAMACHI M U, RAMYA S, et al. Corrosion behaviour of AISI type 304L stainless steel in nitric acid media containing oxidizing species[J]. Corrosion Science, 2011, 53(1): 64-70.
【3】商佳程, 王晓敏, 盛钟琦. Ti 35钛合金与低碳不锈钢在硝酸溶液中的电化学腐蚀对比研究[J]. 中国核科技报告, 2006(1): 14-20.
【4】王凤平, 康万利, 敬和民, 等. 腐蚀电化学原理、方法及应用[M]. 北京: 化学工业出版社, 2008.
【5】曹楚南. 腐蚀电化学原理[M]. 北京: 化学工业出版社, 2004.
【6】史美伦. 交流阻抗谱原理及应用[M]. 北京: 国防工业出版社, 2001.
【7】王玮, 赵吉庆, 张启富. 000Cr25Ni20奥氏体不锈钢在硝酸溶液中的腐蚀电化学行为[J]. 腐蚀与防护, 2010, 31(12): 939-941.
【8】PADHY N, NINGSHEN S, PANIGRAHI B K, et al. Corrosion behaviour of nitrogen ion implanted AISI type 304L stainless steel in nitric acid medium[J]. Corrosion Science, 2010, 52(1): 104-112.
【9】范光伟, 张寿禄, 秦丽雁. 304不锈钢晶间腐蚀发展过程的阻抗谱分析[J]. 铸造设备研究, 2007(3): 12-15.
【10】许淳淳, 徐瑞芬, 欧阳维真, 等. 用交流阻抗法研究形变诱发马氏体相变的1Cr18Ni9Ti不锈钢在酸性NaCl溶液中的孔蚀敏感性[J]. 腐蚀科学与防护技术, 1997, 9(2): 95-102.
【11】陈宇, 陈旭, 刘彤, 等. 温度对316L不锈钢在硼酸溶液中腐蚀电化学行为的影响[J]. 腐蚀与防护, 2014, 35(4): 344-347.
【2】NINGSHEN S, KAMACHI M U, RAMYA S, et al. Corrosion behaviour of AISI type 304L stainless steel in nitric acid media containing oxidizing species[J]. Corrosion Science, 2011, 53(1): 64-70.
【3】商佳程, 王晓敏, 盛钟琦. Ti 35钛合金与低碳不锈钢在硝酸溶液中的电化学腐蚀对比研究[J]. 中国核科技报告, 2006(1): 14-20.
【4】王凤平, 康万利, 敬和民, 等. 腐蚀电化学原理、方法及应用[M]. 北京: 化学工业出版社, 2008.
【5】曹楚南. 腐蚀电化学原理[M]. 北京: 化学工业出版社, 2004.
【6】史美伦. 交流阻抗谱原理及应用[M]. 北京: 国防工业出版社, 2001.
【7】王玮, 赵吉庆, 张启富. 000Cr25Ni20奥氏体不锈钢在硝酸溶液中的腐蚀电化学行为[J]. 腐蚀与防护, 2010, 31(12): 939-941.
【8】PADHY N, NINGSHEN S, PANIGRAHI B K, et al. Corrosion behaviour of nitrogen ion implanted AISI type 304L stainless steel in nitric acid medium[J]. Corrosion Science, 2010, 52(1): 104-112.
【9】范光伟, 张寿禄, 秦丽雁. 304不锈钢晶间腐蚀发展过程的阻抗谱分析[J]. 铸造设备研究, 2007(3): 12-15.
【10】许淳淳, 徐瑞芬, 欧阳维真, 等. 用交流阻抗法研究形变诱发马氏体相变的1Cr18Ni9Ti不锈钢在酸性NaCl溶液中的孔蚀敏感性[J]. 腐蚀科学与防护技术, 1997, 9(2): 95-102.
【11】陈宇, 陈旭, 刘彤, 等. 温度对316L不锈钢在硼酸溶液中腐蚀电化学行为的影响[J]. 腐蚀与防护, 2014, 35(4): 344-347.
相关信息