静液挤压制备的AZ80镁合金管材的腐蚀行为
Corrosion Behavior of AZ80 Magnesium Alloy Tube Fabricated by Hydrostatic Extrusion
摘 要
采用浸泡腐蚀试验、失重腐蚀试验以及电化学方法等研究了静液挤压AZ80镁合金在pH 6.1的0.1 mol/L Na2SO4溶液中的腐蚀行为。结果表明, 静液挤压使得AZ80镁合金晶粒尺寸变小且变形不均匀, 降低了镁合金在含硫介质中的耐蚀性, 表现为浸泡试验中更严重的表面腐蚀形貌、失重试验中更大的平均腐蚀速率、极化曲线中更大的腐蚀电流密度以及电化学阻抗谱中更低的极化电阻。这主要是因为静液挤压变形使得AZ80镁合金内部存在大量的位错缠结, 这样产生的残余内应力会增大镁合金的电化学活性, 降低镁合金的耐蚀性。
静液挤压
位错缠结
耐蚀性
AZ80 magnesium alloy
hydrostatic extrusion
dislocation tangle
corrosion resistance
Abstract
The corrosion behavior of hydrostatically extruded tube AZ80 magnesium alloy in 0.1 mol/L Na2SO4 solution with pH value of 6.1 was investigated by immersion corrosion, weight loss corrosion, and electchemical methods. The results indicated that the corrosion resistance of AZ80 magnesium alloy decreesed because of small grain size and uneven deformation, with more serious corrosion morphology, bigger average corrosion rate, larger corrosion current density in the polarization curves and lower corrosion resistance in the electrochemical impedance spectroscopy plots. This was mainly because of the hydrostatic extrusion which made AZ80 magnesium alloy have large numbers of dislocation tangles. So the residual stress increased the electrochemical activity of magnesium alloy and thus reduced the corrosion resistance of the magnesium alloy.
中图分类号 TG174.2 TG146.2 DOI 10.11973/fsyfh-201510012
所属栏目 试验研究
基金项目
收稿日期 2014/10/10
修改稿日期
网络出版日期
作者单位点击查看
备注吴多祥(1987-), 硕士研究生, 从事镁合金复杂结构零件超高压热流变高效控制成形技术,
引用该论文: WU Duo-xiang,WU Zhi-lin,YUAN Ren-shu,ZHAO Lei,ZHAO Yan-bao. Corrosion Behavior of AZ80 Magnesium Alloy Tube Fabricated by Hydrostatic Extrusion[J]. Corrosion & Protection, 2015, 36(10): 957
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】巫瑞智, 张景怀, 尹东松. 先进镁合金制备与加工技术[M]. 北京: 科学出版社, 2012.
【2】CLOW B B. Magnesium industry overview[J]. Advanced Materials Process, 1996, 150(4): 33-34.
【3】余琨, 黎文献, 王日出. 变形镁合金的研究、开发及应用[J]. 中国有色金属学报, 2003, 13(2): 277-288.
【4】宋光铃. 镁合金腐蚀与防护[M]. 北京: 化学工业出版社, 2006.
【5】王富耻, 张朝晖. 静液挤压技术[M]. 北京: 国防工业出版社, 2008.
【6】徐萍, 刘生发, 黄尚宇, 等. AZ91镁合金显微组织对腐蚀性能的影响[J]. 中国铸造装备与技术, 2004, 4(4): 9-13.
【7】付振南, 熊守美. 铸造镁合金AZ91D金相腐蚀方法研究[J]. 特种铸造及有色合金, 2007, 27(7): 496-498.
【8】周学华, 卫中领, 陈秋荣, 等. 含稀土耐蚀Mg-9Al铸造镁合金腐蚀行为研究[J]. 腐蚀与防护, 2006, 27(10): 487-491.
【9】徐永东, 周灵展, 赵国田, 等. 耐蚀铸造镁合金的研究现状[J]. 兵器材料科学与工程, 2009, 32(6): 84-88.
【10】张新, 李永军, 张奎, 等. Mg-Y镁合金在3.5% NaCl溶液中的腐蚀和电化学行为[J]. 中国有色金属学报, 2013, 23(5): 1226-1236.
【11】丁文江, 向亚贞, 常建卫, 等. Mg-Al系和Mg-RE系合金在NaCl溶液中的腐蚀电化学行为[J]. 中国有色金属学报, 2009, 19(10): 1713-1719.
【12】白丽群, 舒康颖, 李荻, 等. 镁合金AZ91D在氯化钠溶液中的腐蚀行为[J]. 航空材料学报, 2010, 30(1): 62-66.
【13】JB/T 7901-1999金属材料实验室均匀腐蚀全浸试验方法[S].
【14】林翠, 李晓刚. 镁合金在含大气环境中的初期腐蚀行为[J]. 中国有色金属学报, 2004, 14(10): 1658-1665.
【15】BAUMGARTNER M, KAESCHE H. Aluminum pitting in chloride solutions: Morphology and pit growth kinetics[J]. Corrosion Science, 1990, 31: 231-236.
【16】ZHANG C H, HUANG X H, ZHANG M L. Electrochemical characterization of the corrosion of a Mg-Li Alloy[J]. Materials Letters, 2008, 62(14): 2177-2180.
【17】SHI A, SHAW B A, SIKORA E. The role of grain boundary regions in the localized corrosion of a copper-free 6111-like aluminum alloy[J]. Corrosion, 2005, 61(6): 534-548.
【18】古特曼. 金属力学化学与腐蚀防护[M]. 金石译. 北京: 科学出版社, 1989: 48-75.
【19】SONG G L, ATRENS A, WU X L. Corrosion behavior of AZ21, AZ501 and AZ91 in sodium chloride[J]. Corrosion Science, 1998, 40(10): 1769-1791.
【20】SONG G L, ATRENS A, JOHN D S, et al. The anodic dissolution of magnesium in chloride and sulphate solutions[J]. Corrosion Science, 1997, 39(11/12): 1981-2004.
【2】CLOW B B. Magnesium industry overview[J]. Advanced Materials Process, 1996, 150(4): 33-34.
【3】余琨, 黎文献, 王日出. 变形镁合金的研究、开发及应用[J]. 中国有色金属学报, 2003, 13(2): 277-288.
【4】宋光铃. 镁合金腐蚀与防护[M]. 北京: 化学工业出版社, 2006.
【5】王富耻, 张朝晖. 静液挤压技术[M]. 北京: 国防工业出版社, 2008.
【6】徐萍, 刘生发, 黄尚宇, 等. AZ91镁合金显微组织对腐蚀性能的影响[J]. 中国铸造装备与技术, 2004, 4(4): 9-13.
【7】付振南, 熊守美. 铸造镁合金AZ91D金相腐蚀方法研究[J]. 特种铸造及有色合金, 2007, 27(7): 496-498.
【8】周学华, 卫中领, 陈秋荣, 等. 含稀土耐蚀Mg-9Al铸造镁合金腐蚀行为研究[J]. 腐蚀与防护, 2006, 27(10): 487-491.
【9】徐永东, 周灵展, 赵国田, 等. 耐蚀铸造镁合金的研究现状[J]. 兵器材料科学与工程, 2009, 32(6): 84-88.
【10】张新, 李永军, 张奎, 等. Mg-Y镁合金在3.5% NaCl溶液中的腐蚀和电化学行为[J]. 中国有色金属学报, 2013, 23(5): 1226-1236.
【11】丁文江, 向亚贞, 常建卫, 等. Mg-Al系和Mg-RE系合金在NaCl溶液中的腐蚀电化学行为[J]. 中国有色金属学报, 2009, 19(10): 1713-1719.
【12】白丽群, 舒康颖, 李荻, 等. 镁合金AZ91D在氯化钠溶液中的腐蚀行为[J]. 航空材料学报, 2010, 30(1): 62-66.
【13】JB/T 7901-1999金属材料实验室均匀腐蚀全浸试验方法[S].
【14】林翠, 李晓刚. 镁合金在含大气环境中的初期腐蚀行为[J]. 中国有色金属学报, 2004, 14(10): 1658-1665.
【15】BAUMGARTNER M, KAESCHE H. Aluminum pitting in chloride solutions: Morphology and pit growth kinetics[J]. Corrosion Science, 1990, 31: 231-236.
【16】ZHANG C H, HUANG X H, ZHANG M L. Electrochemical characterization of the corrosion of a Mg-Li Alloy[J]. Materials Letters, 2008, 62(14): 2177-2180.
【17】SHI A, SHAW B A, SIKORA E. The role of grain boundary regions in the localized corrosion of a copper-free 6111-like aluminum alloy[J]. Corrosion, 2005, 61(6): 534-548.
【18】古特曼. 金属力学化学与腐蚀防护[M]. 金石译. 北京: 科学出版社, 1989: 48-75.
【19】SONG G L, ATRENS A, WU X L. Corrosion behavior of AZ21, AZ501 and AZ91 in sodium chloride[J]. Corrosion Science, 1998, 40(10): 1769-1791.
【20】SONG G L, ATRENS A, JOHN D S, et al. The anodic dissolution of magnesium in chloride and sulphate solutions[J]. Corrosion Science, 1997, 39(11/12): 1981-2004.
相关信息