MgO@SiO2固化无机磷酸盐防腐蚀涂层材料的制备与研究
Preparation and Research of an Inorganic Phosphate Anticorrosive Coating with MgO@SiO2 Curing Agent
摘 要
以磷酸盐胶黏剂为成膜基料, MgO@SiO2为固化剂制备出一种低温固化无机磷酸盐防腐蚀涂料。以采用纳米颗粒表面包覆技术制备的MgO@SiO2作为固化剂, 实现涂料固化过程中MgO的延缓释放, 在有效延长涂料固化时间的同时降低了固化温度。利用TEM对MgO@SiO2包覆结构进行表征, 借助XRD、SEM、IR、盐雾试验测试、色漆运动粘度测试等手段研究了涂层的物相组成、微观形貌、价键结构、耐盐雾性能和涂料的适用时间, 并深入探究了其固化机理。结果表明, 以MgO@SiO2作为无机磷酸盐涂料固化剂, 涂料固化时间由十几秒延长至120 min以上, 完全固化温度降至80 ℃, 最终所得涂层表面平整致密, 具有较优异的耐吸湿性和防腐蚀性能。
MgO@SiO2
磷酸盐涂层
低温固化
固化机理
coating of nano-particles
MgO@SiO2
phosphate coating
low-temperature curing
curing mechanism
Abstract
A kind of low-temperature cured inorganic phosphate coating composed of phosphate adhesive (film-forming resin) and MgO@SiO2 (curing agent) was prepared. MgO@SiO2, as curing agent, was derived by surface coating mechanisms of nano-particles to realize the gradual-release of MgO in the curing process of the coating. Not only it can increase the curing time but also can decrease the curing temperature of the coating. The MgO@SiO2 was observed by TEM, the micro-morphology, phase composition, chemical bonds, corrosion resistance and pot life of the coating were investigated using SEM, XRD, FTIR, salt spray testing and kinematic viscosity testing. Besides, the curing mechanism of the coating was also explored. Results show that, by selecting MgO@SiO2 as curing agent of the phosphate coating, the curing time of the inorganic phosphate coating was extended from tens of seconds to 120mins, and the curing temperature was decreased to 80 ℃. The prepared coating also has good moisture absorption resistance and corrosion resistance.
中图分类号 TG174.45 TQ630.4 DOI 10.11973/fsyfh-201510015
所属栏目 应用技术
基金项目 海南省自然科学基金(512115); 海南大学服务地方项目(HDSF201308); 海南省重大科技项目(ZDZX2013002)
收稿日期 2014/11/7
修改稿日期
网络出版日期
作者单位点击查看
备注丁春华(1977-), 讲师, 博士, 从事涂料及催化材料研究,
引用该论文: XU San-qiang,DING Chun-hua,WANG Guo-qing,JIANG Hong,LI Jiang,WANG Pei-qing. Preparation and Research of an Inorganic Phosphate Anticorrosive Coating with MgO@SiO2 Curing Agent[J]. Corrosion & Protection, 2015, 36(10): 972
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】杜新胜, 于晓灵, 杨威洁, 等. 防腐涂料的研究与发展[J]. 上海涂料, 2009, 47(7): 26-28.
【2】胡涛, 石莹莹, 周云, 等. 重防腐涂料的应用研究[J]. 现代涂料与涂装, 2008, 11(1): 1-4.
【3】冯海猛, 王力. 有机硅耐高温涂料的研究进展[J]. 化学文摘, 2008(6): 29-30.
【4】陈中华, 石亚军. 水性防腐涂料的研究进展[J]. 应用化工, 2008, 37(12): 1486-1490.
【5】王亦工, 陈华辉, 裴嵩峰, 等. 水性无机硅酸锌防腐涂料的研究进展[J]. 腐蚀科学与防护技术, 2006, 18(1): 41-45.
【6】焦方方, 陈效华, 卢磊. 无机涂料的研究进展[J]. 新材料产业, 2010(6): 50-53.
【7】周锡荣, 唐绍裘, 周武艺. 新型无机涂料的制备及其应用[J]. 山东陶瓷, 2004, 27(1): 17-19.
【8】ROTHON R N. Solution-deposited metal phosphate coatings[J]. Thin Solid Films, 1981, 77(1/3): 149-154.
【9】张雪芹, 徐峰. 无机建筑涂料的研究与发展[J]. 新型建筑材料, 2004(7): 33-37.
【10】董柳杉, 罗瑞盈. 耐高温胶黏剂的研究进展[J]. 炭素技术, 2013, 32(3): 5-8.
【11】陈孜, 张雷, 周科朝, 等. 磷酸盐基耐高温无机黏结剂的研究发展[J]. 粉末冶金材料科学与工程, 2009, 14(2): 74-81.
【12】FEMANDO J A, CHUING D D L. Improving an alumina filter membrane for hot gas filtration using an acid phosphate binder[J]. Journal and Material Science, 2001, 336: 5079-5085.
【13】张振兴, 张彦彬. 材料级磷酸二氢铝的生产与应用[J]. 化工时刊, 2011, 25(9): 20-22.
【14】杨文冬, 黄剑锋, 曹丽云, 等. 磷酸铝的制备及其应用[J]. 无机盐工业, 2009, 41(4): 1-3.
【15】王政阅. 磷酸盐耐热涂层的制备及固化机理的研究[D]. 天津: 天津大学, 2007.
【16】鲍光辉. 磷酸盐胶粘涂层制备及结合性能研究[D]. 天津: 河北工业大学, 2007.
【17】盘荣俊, 何宝林. 纳米颗粒表面包覆技术[J]. 化学与生物工程, 2005(7): 40-42.
【18】DENG Y H, QI D W. Superparamagnetic high-magnetization microspheres with an Fe3O4@SiO2 core and perpendicularly aligned mesoporous SiO2 shell for removal of microcystins[J]. Journal of Amerrican Chemical Society Communications, 2008, 130: 28-29.
【19】CHE S, GARCIA-BENNETT A E, YOKOI T. A novel anionic surfactant templating route for synthesizing mesoporous silica with unique structure[J]. Nature Materials, 2003(2): 801-805.
【20】GARCIA-BENNETT A E, TERASAKI O, CHE S. Structural investigations of AMS-n mesoporous materials by transmission electron microscopy[J]. Chemistry of Materials, 2004, 16(5): 813-821.
【21】李新柱. 杂原子介孔磷酸铝分子筛的合成、表征及催化氧化性能研究[D]. 南京: 南京理工大学, 2012.
【22】冯利利, 朱岳麟, 齐兴义, 等. MgAPO-5分子筛的合成与表征[J]. 石油化工, 2008, 37(4): 344-349.
【2】胡涛, 石莹莹, 周云, 等. 重防腐涂料的应用研究[J]. 现代涂料与涂装, 2008, 11(1): 1-4.
【3】冯海猛, 王力. 有机硅耐高温涂料的研究进展[J]. 化学文摘, 2008(6): 29-30.
【4】陈中华, 石亚军. 水性防腐涂料的研究进展[J]. 应用化工, 2008, 37(12): 1486-1490.
【5】王亦工, 陈华辉, 裴嵩峰, 等. 水性无机硅酸锌防腐涂料的研究进展[J]. 腐蚀科学与防护技术, 2006, 18(1): 41-45.
【6】焦方方, 陈效华, 卢磊. 无机涂料的研究进展[J]. 新材料产业, 2010(6): 50-53.
【7】周锡荣, 唐绍裘, 周武艺. 新型无机涂料的制备及其应用[J]. 山东陶瓷, 2004, 27(1): 17-19.
【8】ROTHON R N. Solution-deposited metal phosphate coatings[J]. Thin Solid Films, 1981, 77(1/3): 149-154.
【9】张雪芹, 徐峰. 无机建筑涂料的研究与发展[J]. 新型建筑材料, 2004(7): 33-37.
【10】董柳杉, 罗瑞盈. 耐高温胶黏剂的研究进展[J]. 炭素技术, 2013, 32(3): 5-8.
【11】陈孜, 张雷, 周科朝, 等. 磷酸盐基耐高温无机黏结剂的研究发展[J]. 粉末冶金材料科学与工程, 2009, 14(2): 74-81.
【12】FEMANDO J A, CHUING D D L. Improving an alumina filter membrane for hot gas filtration using an acid phosphate binder[J]. Journal and Material Science, 2001, 336: 5079-5085.
【13】张振兴, 张彦彬. 材料级磷酸二氢铝的生产与应用[J]. 化工时刊, 2011, 25(9): 20-22.
【14】杨文冬, 黄剑锋, 曹丽云, 等. 磷酸铝的制备及其应用[J]. 无机盐工业, 2009, 41(4): 1-3.
【15】王政阅. 磷酸盐耐热涂层的制备及固化机理的研究[D]. 天津: 天津大学, 2007.
【16】鲍光辉. 磷酸盐胶粘涂层制备及结合性能研究[D]. 天津: 河北工业大学, 2007.
【17】盘荣俊, 何宝林. 纳米颗粒表面包覆技术[J]. 化学与生物工程, 2005(7): 40-42.
【18】DENG Y H, QI D W. Superparamagnetic high-magnetization microspheres with an Fe3O4@SiO2 core and perpendicularly aligned mesoporous SiO2 shell for removal of microcystins[J]. Journal of Amerrican Chemical Society Communications, 2008, 130: 28-29.
【19】CHE S, GARCIA-BENNETT A E, YOKOI T. A novel anionic surfactant templating route for synthesizing mesoporous silica with unique structure[J]. Nature Materials, 2003(2): 801-805.
【20】GARCIA-BENNETT A E, TERASAKI O, CHE S. Structural investigations of AMS-n mesoporous materials by transmission electron microscopy[J]. Chemistry of Materials, 2004, 16(5): 813-821.
【21】李新柱. 杂原子介孔磷酸铝分子筛的合成、表征及催化氧化性能研究[D]. 南京: 南京理工大学, 2012.
【22】冯利利, 朱岳麟, 齐兴义, 等. MgAPO-5分子筛的合成与表征[J]. 石油化工, 2008, 37(4): 344-349.
相关信息