Properties and Effect Factors of Conductive Anticorrosive Coating
摘 要
以湿式电除尘极板为载体, 导电防腐蚀涂料为试验原料, 探寻湿式电除尘在运行过程中出现的极板腐蚀问题以及针对湿式电除尘器导电防腐蚀涂料的性能, 研究涂料在不同厚度、不同涂刷次数、不同烘干时间下对涂膜硬度、附着力、电阻率等特性的影响; 以及涂膜的耐酸、耐碱、耐盐和耐水性。通过理论分析及试验研究, 确定涂料的防腐蚀性能参数和最佳涂抹方式。结果表明, 除尘极板导电防腐蚀涂料最佳涂抹方式为涂膜的厚度不低于0.14 mm, 最佳涂刷次数为3次, 涂膜烘干温度为60 ℃, 烘干时间为12 h。
Abstract
With wet electric dust plate as the carrier, conductive coatings as experimental materials, the corrosion of wet electric dust plate during its operation and the performance of conductive anticorrosive coatings of wet electric dust collector were investigated. The effect of coating thickness, brushing time and drying time on the hardness, adhesion, and specific resistance of coatings was studied. Properties of coatings, including the coating resistance to acid, alkali, salt and water were also studied. Anticorrosive coating corrosion performance parameters and the best way to smear were obtained through a series of tests. The results show that the most optimal parameters were the coating thickness of no less than 0.14 mm, paint times of 3, coating drying temperature of 60℃, and drying hour of 12.
中图分类号 TG174.4 TQ630.4 DOI 10.11973/fsyfh-201510016
所属栏目 应用技术
基金项目 国家资源部煤炭勘查与综合利用重点实验室开放课题(KF205-1); 陕西省教育厅科学研究计划(自然科学专项)项目(2013JK0869); 陕西省科技统筹创新工程计划项目(2012KTZB03-01-02)
收稿日期 2014/12/10
修改稿日期
网络出版日期
作者单位点击查看
备注张蕾(1981-), 副教授, 博士, 从事煤炭加工利用与环境保护技术工作,
引用该论文: ZHANG Lei,SHA Xiang-ling,ZHANG Nian,TIAN Ye,WANG Long-wei,YANG Yan,LV Bao-peng. Properties and Effect Factors of Conductive Anticorrosive Coating[J]. Corrosion & Protection, 2015, 36(10): 978
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】姜泽宇. 烟气净化设备的腐蚀机理和防护方法[J]. 腐蚀与防护, 2005, 26(12): 530-533.
【2】曾庭华. 湿法脱硫系统对锅炉尾部烟道和烟囱影响的研究[J]. 电力建设, 2002, 23(4): 19-22.
【3】WESSLING B. Effective corrosion protection with the organic metal polyaniline: Basic principles and recent progress[J]. Electro active Polymers for Corrosion Control, 2003, 843: 34-73.
【4】BUSATO F. Powder and waterborne coatings 2000-2010 is past growth sustainable[C]//Quo Vadis-Coatings.[S.l.]: [s.n.], 2002: 187-190.
【5】郝文阁, 侯亚平, 赵光玲, 等. 静电除尘器极板涂敷导电防腐涂料对静电除尘性能影响的研究[J]. 环境科学学报, 2008, 28(5): 956-959.
【6】郝文阁. 水泥厂机立窑用电除尘器研究[J]. 环境工程, 2001, 19(5): 33-35.
【7】GONZALEZ-GARCIA Y, GONZALEZ S, SOUTO R M. Electrochemical and structural properties of a polyurethane coating on steel substrates for corrosion protection[J]. Corros Sci, 2007, 49(9): 3514-3526.
【8】周丹. 纳米导电防腐涂料导电性能影响因素及其制备技术的研究[D]. 哈尔滨: 哈尔滨工业大学, 2008.
【9】谭健斌. 水性沥青防腐涂料的制备与性能研究[D]. 广州: 华南理工大学, 2010.
【10】刘海. 水性环氧涂料制备及防腐性能研究[D]. 沈阳: 沈阳理工大学, 2012.
【2】曾庭华. 湿法脱硫系统对锅炉尾部烟道和烟囱影响的研究[J]. 电力建设, 2002, 23(4): 19-22.
【3】WESSLING B. Effective corrosion protection with the organic metal polyaniline: Basic principles and recent progress[J]. Electro active Polymers for Corrosion Control, 2003, 843: 34-73.
【4】BUSATO F. Powder and waterborne coatings 2000-2010 is past growth sustainable[C]//Quo Vadis-Coatings.[S.l.]: [s.n.], 2002: 187-190.
【5】郝文阁, 侯亚平, 赵光玲, 等. 静电除尘器极板涂敷导电防腐涂料对静电除尘性能影响的研究[J]. 环境科学学报, 2008, 28(5): 956-959.
【6】郝文阁. 水泥厂机立窑用电除尘器研究[J]. 环境工程, 2001, 19(5): 33-35.
【7】GONZALEZ-GARCIA Y, GONZALEZ S, SOUTO R M. Electrochemical and structural properties of a polyurethane coating on steel substrates for corrosion protection[J]. Corros Sci, 2007, 49(9): 3514-3526.
【8】周丹. 纳米导电防腐涂料导电性能影响因素及其制备技术的研究[D]. 哈尔滨: 哈尔滨工业大学, 2008.
【9】谭健斌. 水性沥青防腐涂料的制备与性能研究[D]. 广州: 华南理工大学, 2010.
【10】刘海. 水性环氧涂料制备及防腐性能研究[D]. 沈阳: 沈阳理工大学, 2012.
相关信息