热采锅炉炉管异种钢焊接接头失效原因分析
THE FAILURE ANALYSIS OF THE CRACKED BOILER TUBES
摘 要
利用光谱分析仪、光学显微镜和扫描电镜等测试手段,测试了炉管材料的化学成分和显微硬度,观察了失效接头的金相组织和断口形貌。发现焊接接头处存在魏氏组织、夹杂物严重聚集及局部区域出现熔合不良。分析结果表明,炉管接头焊接工艺参数过大,焊接材料选择不当,是引起炉管焊接接头失效的主要原因。
失效分析
焊接接头
Furnace pipe
Failure analys
Welded joint
Abstract
By using spectrum analyzer,optical microscope and SEM,chemical composition and microhardness of tube material were tested,and metallurgical structure and fracture pattern of the joint were observed. It is found that there was widmanstaten structure in the joint and inclusion aggregated. And part area of the joint lacked of fusion. The analysis showed that overside of parameter in furnace tube joint welding,and unsuitable choices of the welding material were the main reason of the joint failure.
中图分类号 TE934+.5
所属栏目 质量控制与失效分析
基金项目
收稿日期 2006/6/16
修改稿日期
网络出版日期
作者单位点击查看
备注王炳英(1972-),女,副教授,博士研究生。
引用该论文: WANG Bing-ying,LIU Wei-qiang. THE FAILURE ANALYSIS OF THE CRACKED BOILER TUBES[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2007, 43(1): 32～34
王炳英,刘伟强. 热采锅炉炉管异种钢焊接接头失效原因分析[J]. 理化检验－物理分册, 2007, 43(1): 32～34
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】温 涛,张乃峰,卢 鑫,等.热采锅炉炉管爆裂原因分析［J］.金属热处理,2004,29(11):57-59．
【2】温建萍.高温高压注汽管线破裂原因分析［J］.压力容器,2001,18(3):63-66．
【3】赵 哲,王德和,徐卫平.电厂锅炉管道爆破失效分析［J］.理化检验-理化分册,2002,38(2):78-79,82．
【4】GB 5310-1995 高压锅炉用无缝钢管［S］．
【5】周振丰,张文钺.焊接冶金与金属焊接性［M］.北京:机械工业出版社,1992．
【2】温建萍.高温高压注汽管线破裂原因分析［J］.压力容器,2001,18(3):63-66．
【3】赵 哲,王德和,徐卫平.电厂锅炉管道爆破失效分析［J］.理化检验-理化分册,2002,38(2):78-79,82．
【4】GB 5310-1995 高压锅炉用无缝钢管［S］．
【5】周振丰,张文钺.焊接冶金与金属焊接性［M］.北京:机械工业出版社,1992．
相关信息