COMPARISON OF TC4 TITANIUM ALLOY AND MODIFIED SURFACES ANTIBACTERIAL PROPERTY BY BACTERIAL ADHESION METHOD
摘 要
对牙种植体用材料TC4(Ti6Al4V)进行不同工艺的表面改性处理。应用细菌粘附方法,在荧光显微镜下直接计数,观察未处理试样和不同工艺处理后试样表面的细菌粘附,以评价改性表面的抗菌能力;同时采用SPSS统计软件分析对比两种工艺处理后改性表面的抗菌能力。细菌粘附和统计结果显示,未处理试样表面粘附了大量细菌;处理后试样表面粘附数量已显著减少;两种处理工艺改性后的表面之间细菌粘附量的差别没有统计学差异,即两种工艺处理后的改性表面的抗菌能力没有显著的差异。
Abstract
Titanium alloy TC4 (Ti6Al4V) used as dental implant materials were modified by different surface modification technologies. The bacterial adhesion method and the tagging effect of fluorescence were employed to evaluate antibacterial property of modified surfaces by observing bacterial adhesion status and counting quantities of bacterial adhesion on the Ti6Al4V surfaces below the fluorescence microscope;SPSS software was used to analysis and compare the antibacterial property of modified surfaces at the same time. The bacterial adhesion assay and statistic analysis results showed that: compared to the unmodified surface,both of ion nitriding-treated and ion plating-treated specimen surfaces could reduce bacterial adhesion significantly,and also there were no obvious differences between the two modification technologies treated surfaces at quantities of bacterial adhesion by statistic analysis,which means there were no obvious differences between the two modified processes treated surfaces at antibacterial property.
中图分类号 TG174.4 R783.1
所属栏目 实验技术与方法
基金项目 国家自然科学基金(50501016);山西省自然科学基金(20051049);山西省自然科学基金(2006021023)
收稿日期 2006/9/6
修改稿日期
网络出版日期
作者单位点击查看
备注林乃明(1981-),男,硕士研究生。
引用该论文: LIN Nai-ming,QU Jun-zhi,PAN Fu-qin,FAN Ai-lan,QIN Lin,TANG Bin. COMPARISON OF TC4 TITANIUM ALLOY AND MODIFIED SURFACES ANTIBACTERIAL PROPERTY BY BACTERIAL ADHESION METHOD[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2007, 43(3): 134~136
林乃明,曲均志,潘福勤,范爱兰,秦 林,唐 宾. 用细菌粘附法比较TC4钛合金及其表面改性后的抗菌能力[J]. 理化检验-物理分册, 2007, 43(3): 134~136
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】但智钢,倪红卫,许伯藩,等.铜离子注入马氏体不锈钢的抗菌性能研究[J].功能材料,2004,35(4):527-528.
【2】张玉梅,郭天文,李佐臣.钛及钛合金在口腔科应用的研究方向[J].生物医学工程学杂志,2000,17(2):206-208.
【3】何宝明.生物医用钛及其合金材料的开发应用进展、市场状况及问题分析[J].新材料产业,2003,116(7):23-28.
【4】储成林,朱景川,尹钟大.医用钛合金及其表面改性[J].材料科学与工艺,1998,6(2):40-44.
【5】刘天佳主编.口腔疾病的微生物学基础[M].1版.北京:人民卫生出版社,1999:65-73.
【6】黄定明.变形链球菌的粘附机理[J].国外医学-口腔医学分册,1994,21(3):132-135.
【7】刘劲松,高 宁.细菌在牙种植体表面的定植及影响因素[J].国外医学-口腔医学分册,2004,S1:121-124.
【8】潘福勤.两种不同表面处理对钛及钛合金抗菌性能影响的研究[D].山西太原:山西医科大学硕士学位论文,2006.
【9】李笑梅,郭天文,周中华,等.五种常用口腔修复材料对细菌滞留影响的临床研究[J].上海第二军医大学学报,2002,23(1):81-83.
【10】施小茹,冷 赢,韩丽娜,等.人工晶体细菌粘附实验研究[J].白求恩医科大学学报,2001,27(4):369-370.
【11】Catledge S A,Vohra Y K,Bellis S L,et al. Mesenchymal stem cell adhesion and spreading on nanostructured biomaterials [J]. Nanosci Nanotechnology,2004,4(8):986-990.
【12】Yoshinari M,Oda Y,Kato T,et al. Influence of surface modifications to titanium on antibacterial activity in vitro [J]. Biomaterials,2001,22(14):2043-2048.
【13】Scarano A,Piattelli M,Vrespa G,et al. Bacterial adhesion on titanium nitride-coated and uncoated implants: an in vivo human study [J]. Oral Implntol,2003,29(2):80-85.
【2】张玉梅,郭天文,李佐臣.钛及钛合金在口腔科应用的研究方向[J].生物医学工程学杂志,2000,17(2):206-208.
【3】何宝明.生物医用钛及其合金材料的开发应用进展、市场状况及问题分析[J].新材料产业,2003,116(7):23-28.
【4】储成林,朱景川,尹钟大.医用钛合金及其表面改性[J].材料科学与工艺,1998,6(2):40-44.
【5】刘天佳主编.口腔疾病的微生物学基础[M].1版.北京:人民卫生出版社,1999:65-73.
【6】黄定明.变形链球菌的粘附机理[J].国外医学-口腔医学分册,1994,21(3):132-135.
【7】刘劲松,高 宁.细菌在牙种植体表面的定植及影响因素[J].国外医学-口腔医学分册,2004,S1:121-124.
【8】潘福勤.两种不同表面处理对钛及钛合金抗菌性能影响的研究[D].山西太原:山西医科大学硕士学位论文,2006.
【9】李笑梅,郭天文,周中华,等.五种常用口腔修复材料对细菌滞留影响的临床研究[J].上海第二军医大学学报,2002,23(1):81-83.
【10】施小茹,冷 赢,韩丽娜,等.人工晶体细菌粘附实验研究[J].白求恩医科大学学报,2001,27(4):369-370.
【11】Catledge S A,Vohra Y K,Bellis S L,et al. Mesenchymal stem cell adhesion and spreading on nanostructured biomaterials [J]. Nanosci Nanotechnology,2004,4(8):986-990.
【12】Yoshinari M,Oda Y,Kato T,et al. Influence of surface modifications to titanium on antibacterial activity in vitro [J]. Biomaterials,2001,22(14):2043-2048.
【13】Scarano A,Piattelli M,Vrespa G,et al. Bacterial adhesion on titanium nitride-coated and uncoated implants: an in vivo human study [J]. Oral Implntol,2003,29(2):80-85.
相关信息