余热锅炉热交换管破裂原因分析
FRACTURE ANALYSIS OF THE PIPES FOR EXCHANGING BOILER′S SURPLUS HEAT
摘 要
采用化学成分、显微组织、裂纹及断口特征等方法对余热锅炉热交换管破裂原因进行了分析。结果表明,热交换管破裂是烟道气流对管道的腐蚀和冲蚀磨损的结果。建议采用具有抗蚀能力的高温材料并控制烟道气硫和氧的含量。
热交换
腐蚀
Failure analysis
Heat exchanging
Erosion
Abstract
In this paper,the failure reason of the pipes transporting boiler′s surplus heat are analyzed. After a comprehensive study on chemical composition,microsturcture,fractures and cracks,the results show that the fractures occured under the effects of combined freting and erosion of the airflow from the flue,it is suggested to use steel with high temperature strength and high anti-erosion,at the same time,strictly controlling the content of sulfur and oxygen in the flue is necessary.
中图分类号 TK229.92+9
所属栏目 质量控制与失效分析
基金项目 广东省自然科学基金资助项目(04300026);华南理工大学自然科学基金资助项目(200532)
收稿日期 2006/4/24
修改稿日期
网络出版日期
作者单位点击查看
备注陈 灵(1971-),女,工程师,硕士。
引用该论文: CHEN Ling,LIANG Si-zu,LIU Zheng-yi,WU Zhi-wei. FRACTURE ANALYSIS OF THE PIPES FOR EXCHANGING BOILER′S SURPLUS HEAT[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2007, 43(3): 144～146
陈 灵,梁思祖,刘正义,吴志伟. 余热锅炉热交换管破裂原因分析[J]. 理化检验－物理分册, 2007, 43(3): 144～146
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】GB 3077-1978 合金结构钢号及化学成分［S］．
【2】刘正义,吴连生,许麟康,等.机械装备失效分析图谱［M］.广州:广东科技出版社,1990．
【3】周永欣,吕振林,张 敏,等.30CrMo钢泵体开裂失效分析［J］.机械工程材料,2004,28(9):52-54．
【2】刘正义,吴连生,许麟康,等.机械装备失效分析图谱［M］.广州:广东科技出版社,1990．
【3】周永欣,吕振林,张 敏,等.30CrMo钢泵体开裂失效分析［J］.机械工程材料,2004,28(9):52-54．
相关信息