储气塔阀门紧固螺栓的断裂分析
FAILURE ANALYSIS OF THE FASTENING BOLT OF THE VALVE ON THE GAS TOWER
摘 要
储气塔运行半年即发生了阀门紧固螺栓的断裂事故。采用化学成分分析、硬度测定、金相检验以及断口的宏、微分析等方法,对螺栓断裂原因进行了分析。结果表明,由于塔内腐蚀性介质的微量渗出,导致了阀门紧固螺栓的应力腐蚀断裂。
脆性断口
应力腐蚀
断裂
Fastening bolt
Brittle fracture
Stress crrosion
Crack
Abstract
Fastening bolts at valve on gas tower was cracked after used 6 months. The failure analysis of the bolt was made by chemical composition,hardness,microstrcture examination and macrostrcture,SEM,EDX analysis for the fracture. The results show that the stress crrosion,wich is duo to the less leaking of the crrosion media in tower,cause the fastening bolt of valve failure.
中图分类号 TE986
所属栏目 质量控制与失效分析
基金项目
收稿日期 2006/8/22
修改稿日期
网络出版日期
作者单位点击查看
备注谷志刚(1954-),男,教授级高级工程师,学士。
引用该论文: GU Zhi-gang,HAO De-zhong,LI Wei-hang. FAILURE ANALYSIS OF THE FASTENING BOLT OF THE VALVE ON THE GAS TOWER[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2007, 43(3): 147～149
谷志刚,郝德中,李伟航. 储气塔阀门紧固螺栓的断裂分析[J]. 理化检验－物理分册, 2007, 43(3): 147～149
被引情况:
【1】王兆希,郭宏梅,张小亮,於旻, "电站稳压器支承裙座锚固螺栓断裂失效分析",理化检验－物理分册 51, 747-750(2015)
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】廖景娱,刘正义编.金属构件失效分析［M］.北京:化学工业出版社,2003:101．
【2】赵麦群,雷阿丽编.金属的腐蚀与防护［M］.北京:国防工业出版社,2002:9．
【3】［前苏］瓦西连科,麦列霍夫著.陈石卿,焦明山译.钢的应力腐蚀开裂［M］.北京:国防工业出版社,1983:97．
【4】姚红宇.腐蚀环境作用下失效的失效分析［J］.理化检验-物理分册,2005,41(11):590-593．
【2】赵麦群,雷阿丽编.金属的腐蚀与防护［M］.北京:国防工业出版社,2002:9．
【3】［前苏］瓦西连科,麦列霍夫著.陈石卿,焦明山译.钢的应力腐蚀开裂［M］.北京:国防工业出版社,1983:97．
【4】姚红宇.腐蚀环境作用下失效的失效分析［J］.理化检验-物理分册,2005,41(11):590-593．
相关信息