镀锌钢板受热变色的原因分析
ANALYSIS OF SURFACE DISCOLORATION OF GALVANIZING SHEET STEEL CAUSED BY UNFAVORABLE BRAZING HEATING
摘 要
用体视显微镜和电镜研究了空调机内部铜管在钎焊过程中镀锌端板发生黑、白变色的原因。结果表明,镀锌板局部变色是钎焊火焰加热而形成Zn-Fe合金所致。黑色区域表面存在细小裂纹,在盐雾实验时表现出低的抗蚀性能。
颜色
加热
失效分析
Galvanizing sheet steel
Colour
Heating
Failure analysis
Abstract
The reason of the end of galvanizing sheet steel becoming dark and bright,when copper tube of air conditioner was brazing,was investigated by stereomicroscope and SEM. The result showed that the color changing was caused by Zn-Fe alloy in brazing flame heating,it showed that fine cracks existed in dark zone and the end of sheet with low corrosion resistant in salt spray test.
中图分类号 TG174.4
所属栏目 试验与研究
基金项目
收稿日期 2006/3/23
修改稿日期
网络出版日期
作者单位点击查看
备注李大东(1963－),男,高级工程师,硕士研究生。
引用该论文: LI Da-dong,YU Teng-yi. ANALYSIS OF SURFACE DISCOLORATION OF GALVANIZING SHEET STEEL CAUSED BY UNFAVORABLE BRAZING HEATING[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2007, 43(4): 176～178
李大东,余腾义. 镀锌钢板受热变色的原因分析[J]. 理化检验－物理分册, 2007, 43(4): 176～178
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】余金山,张津徐,吴建生,等.汽车用热镀锌钢板镀层的性能综述［J］.理化检验-物理分册,2005,41(7):325-328．
【2】Motaigne Jean-Michel,表明生.汽车用合金化热镀锌钢板的最佳镀层微观结构［J］.世界钢铁,2001,1(6):19-23．
【3】周亚梅,扬 芃.影响IF钢合金化热镀锌钢板成型性和抗粉化性因素的研究［J］.钢铁研究,2001,122(5):45-49．
【2】Motaigne Jean-Michel,表明生.汽车用合金化热镀锌钢板的最佳镀层微观结构［J］.世界钢铁,2001,1(6):19-23．
【3】周亚梅,扬 芃.影响IF钢合金化热镀锌钢板成型性和抗粉化性因素的研究［J］.钢铁研究,2001,122(5):45-49．
相关信息