RESEARCH ON PREVENTION METHOD OF INTERCRYSTALLINE CORROSION FOR 1Cr18Ni9Ti SEAMLESS STEEL PIPE
摘 要
晶间腐蚀是奥氏体不锈钢管最危险的破坏形式之一。通过对晶间腐蚀产生原因的分析,归纳了影响1Cr18Ni9Ti无缝钢管晶间腐蚀的诸多因素,提出防止材料的晶间腐蚀的有效方法为:降低碳及磷、硫等有害杂质元素的含量;添加少量稳定化元素钛,适当增加铬含量,减少镍含量;在1 050~1 100 ℃进行固溶处理,快速冷却,抑制在晶界析出碳化物;在850~880 ℃下进行稳定化处理2~4 h,然后缓慢冷却;在需要进行冷加工和于相当敏化温度处理的场合下,遵循先冷加工,而后进行热处理的原则;通过加工及热处理将晶粒度控制在6~8级。
Abstract
The intercrystalline corrosion is one of the most dangerous destruction forms for austenite stainless steel pipe. Through the reason analysis of the intercrystalline corrosion,many factors are induced which have affected the 1Cr18Ni9Ti seamless steel pipe intercrystalline corrosion. And the effective methods are proposed to prevent the intercrystalline corrosion. There are many effective methods as follows: decreasing the carbon,the phosphorus and harmful impurity element content;Increases the few stable elements titanium,suitably increases the chromium content,reducing the nickel content;In 1 050~1 100℃ carring on the solid solution treatment,the quick speed cools,suppresses separates out the carbide in the crystal boundary;In 850~880℃ under carries on the stable processing for 2~4 h,then slow cooling;In needs to carry on the cold finishing and in under the suitable sensitization temperature processing situation,follows first the cold finishing,after but carries on the heat treatment the principle;Through processing and heat treatment crystal grain size control in 6~8 levels.
中图分类号 TG174
所属栏目 试验技术与方法
基金项目
收稿日期 2005/12/6
修改稿日期
网络出版日期
作者单位点击查看
备注宋 铎(1963-),男,高级工程师,硕士。
引用该论文: SONG Duo. RESEARCH ON PREVENTION METHOD OF INTERCRYSTALLINE CORROSION FOR 1Cr18Ni9Ti SEAMLESS STEEL PIPE[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2007, 43(6): 296~298
宋 铎. 防止1Cr18Ni9Ti无缝钢管晶间腐蚀的方法研究[J]. 理化检验-物理分册, 2007, 43(6): 296~298
被引情况:
【1】赵琼,刘占存,赵明宇, "冷轧普碳黑退钢带不耐酸腐蚀原因及影响因素分析",理化检验-物理分册 47, 493-498(2011)
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
相关信息