40Cr钢轧辊断裂原因分析
FRACTURE ANALYSIS OF 40Cr STEEL ROLL
摘 要
采用化学成分、宏观断口、低倍组织及金相组织等分析方法对轧辊断裂原因进行了分析。结果表明,轧辊冶金质量低劣,化学成分超差,一般斑点状偏析超标及内部气泡严重,而内部气泡是导致轧辊断裂的主要原因。对此提出了相应的措施及建议。
轧辊
气泡
热应力
40Cr
Roll
Blowhole
Thermal stress
Abstract
The reason of roll fracture has been analyzed by means of chemical composition analysis,macro fractograph,low magnification structure and microstructure examination. It′s showed that the roll is of bad quality. For example,chemical composition and general spotted segregation exceed the standard specification. Interior blowhole badly appears,which is the main reason resulting the roll fracture. Thus,corresponding measure and suggestion have been put forward.
中图分类号 TG333.17
所属栏目 质量控制与失效分析
基金项目
收稿日期 2006/9/6
修改稿日期
网络出版日期
作者单位点击查看
备注朱晓红(1965-),女,高级工程师,学士。
引用该论文: ZHU Xiao-hong. FRACTURE ANALYSIS OF 40Cr STEEL ROLL[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2007, 43(6): 314～316
朱晓红. 40Cr钢轧辊断裂原因分析[J]. 理化检验－物理分册, 2007, 43(6): 314～316
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】孙盛玉,戴雅康.热处理裂纹分析图谱［M］.大连:大连出版社,2002:51．
【2】机械性能编写组.金属机械性能［M］.北京:机械工业出版社,1979:69．
【2】机械性能编写组.金属机械性能［M］.北京:机械工业出版社,1979:69．
相关信息