水表连接黄铜螺母断裂分析
FRACTURE ANALYSIS OF CONNECTING BRASS NUT FOR TAP WATER METER
摘 要
居民住宅内与水表连接的黄铜螺母发生断裂,造成管路泄漏。采用宏、微观检验方法对失效螺母进行了分析。结果表明,黄铜材料中含有较多的铅,使金属基体脆化并在晶界上存在脆性共晶体网膜,加上金属中还存在孔洞、缩松等铸造缺陷,是造成螺母断裂的主要原因。
断裂
失效分析
Brass nut
Fracture
Failure analysis
Abstract
The fracture of brass nut for connecting tap and water meter lead to pipeline leakage at a residence. The fracture analysis was made by means of macroscopic and scanning electron microscope. Experiment results showed that the fracture of the nut was caused by foundry defects such as holes,shrinkages .And redundant lead in brass nut which formed fragile eutectic omentum in grain boundary was another reason of the fracture.
中图分类号 TS914.3+3
所属栏目 质量控制与分析
基金项目
收稿日期 2006/8/3
修改稿日期
网络出版日期
作者单位点击查看
备注于利军(1960-),男,高级工程师。
引用该论文: YU Li-jun,SUN Ping,YU Shan-wei. FRACTURE ANALYSIS OF CONNECTING BRASS NUT FOR TAP WATER METER[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2007, 43(7): 376～378
于利军,孙 屏,于善伟. 水表连接黄铜螺母断裂分析[J]. 理化检验－物理分册, 2007, 43(7): 376～378
被引情况:
【1】郭亮,金献忠,黄世杰,张建波,吴薇, "铅黄铜阀芯部件开裂分析",理化检验－物理分册 49, 625-627(2013)
【2】杨晓,张先锋,苗富贵,李雪峰, "H62黄铜套管环境致裂行为分析",理化检验－物理分册 51, 283-285(2015)
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】张 栋.失效分析［M］.北京,国防工业出版社,2004:5．
【2】林肇琦.有色金属材料学［M］.沈阳:东北工学院出版社,1986:7．
【3】韩新利.N80不加厚油管失效分析［J］.理化检验-物理分册,2005,41(z1):324-328．
【2】林肇琦.有色金属材料学［M］.沈阳:东北工学院出版社,1986:7．
【3】韩新利.N80不加厚油管失效分析［J］.理化检验-物理分册,2005,41(z1):324-328．
相关信息