大环件轧机用芯轴断裂分析
ANALYSIS OF THE RUPTURED CORE AXES OF THE ROLL MILL FOR ROLLING BIG RING
摘 要
大环件轧机的芯轴连续发生断裂。采用断口分析、金相检验、电镜能谱分析和力学性能测定的方法对芯轴断裂的原因进行了分析。结果表明,所用材料的显微组织缺陷和耐热性能差是导致芯轴发生早期断裂的主要原因。
显微组织缺陷
耐热性
Core axes
Microstructure defect
Heatproof property
Abstract
The core axes of roll mill had been ruptured continuely. It was investigated by means of fracture analysis,microstructure examination,SEM energy spectrum analysis and mechanical properties testing. The result showed that the defects of the microstructure in the core axes and the poor heatproof of the material were the main reasons for the core axes′s earlier ruptured.
中图分类号 TH133.2
所属栏目 质量控制与失效分析
基金项目
收稿日期 2006/3/31
修改稿日期
网络出版日期
作者单位点击查看
备注杨 峥(1972-),女,高级工程师,学士。
引用该论文: YANG Zheng,CHEN Lian-man,YANG Li-zhu. ANALYSIS OF THE RUPTURED CORE AXES OF THE ROLL MILL FOR ROLLING BIG RING[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2007, 43(8): 411～413
杨 峥,陈联满,杨丽珠. 大环件轧机用芯轴断裂分析[J]. 理化检验－物理分册, 2007, 43(8): 411～413
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】胡世炎编著.破断故障金相分析［M］.北京:国防工业出版社,1979:188．
【2】吴连生.失效分析技术［M］.成都:四川科学技术出版社,1985．
【2】吴连生.失效分析技术［M］.成都:四川科学技术出版社,1985．
相关信息