40Mn18Cr4V钢穿心螺杆断裂分析

40Mn18Cr4V钢穿心螺杆断裂分析

FAILURE ANALYSIS OF 40Mn18Cr4V STEEL BOLT

龙会国

陈红冬

杨湘伟

摘要

穿心螺杆在安装过程中发生断裂失效。采用金相组织检验和扫描电镜显微分析等方法进行了分析。结果表明,由于在该螺杆制造过程中有轴向链状夹杂物存在及各种应力下产生轴向裂纹,最后在受预紧、铁心热膨胀等力作用下,在轴向裂纹尖端应力集中处发生横向脆性断裂。

标签穿心螺杆

断裂

失效分析

Bolt

Fracture

Failure analysis

Abstract

The bolt was ruptured during assembly. The fracture analysis of bolt was carried out by means of microstructure examination and SEM observation. The results showed that,the non-homogeneous distribution of string inclusions and stresses caused axial cracks,which gradually extended till fracture at stress concentration of crack tip under prefastening force and hot expansion action.

中图分类号 TM303

所属栏目质量控制与失效分析

基金项目

收稿日期 2007/2/1

修改稿日期

网络出版日期

作者单位点击查看

备注龙会国(1978-),男,助工,工学硕士。

引用该论文: LONG Hui-guo,CHEN Hong-dong,YANG Xiang-wei. FAILURE ANALYSIS OF 40Mn18Cr4V STEEL BOLT[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2007, 43(11): 583～586
龙会国,陈红冬,杨湘伟. 40Mn18Cr4V钢穿心螺杆断裂分析[J]. 理化检验－物理分册, 2007, 43(11): 583～586

论文评价

共有人对该论文发表了看法，其中：

人认为该论文很差

人认为该论文较差

人认为该论文一般

人认为该论文较好

人认为该论文很好

分享论文

参考文献

【1】姜求志,王金瑞.火力发电厂金属材料手册［M］.北京:中国电力出版社,2000:647-648．

相关信息

	标题	相关频次
	柴油机用高强度螺栓断裂失效分析	5
	电站稳压器支承裙座锚固螺栓断裂失效分析	5
	液氨储存罐304不锈钢法兰连接螺栓断裂失效分析	5
	主汽门阀盖螺栓断裂失效分析	5
	252 kV GIS机构止动螺栓的断裂失效分析	4
	30CrMnSiA钢螺钉断裂失效分析	4
	3Cr2W8V钢压铸模具断裂分析	4
	40Cr钢汽车半轴断裂失效分析	4
	TP304H奥氏体锅炉管高温运行显微特征	4
	TP347H耐热钢管在超临界条件下的氧化膜结构及形成机理	4
	抽油泵凡尔罩断裂失效分析	4
	船用艉轴断裂失效分析	4
	电站连接螺栓断裂失效分析	4
	吊装过程中吊具断裂失效分析	4
	断裂油管失效分析	4
	高强度螺栓断裂失效分析	4
	高强度套管断裂失效预防及标准化	4
	锅炉高温过热器弯管的失效分析	4
	锅炉水冷壁管沉积物下腐蚀损伤特征及其超声检测	4
	锅炉水冷壁管沉积物下氧化腐蚀特征及其机理	4
	恒速传动装置齿轮断裂失效分析	4
	铝合金焊缝超声波检测工艺参数的选择	4
	某卡箍连接片断裂失效分析	4
	某汽车换档摇臂断裂失效分析	4
	某塔吊钢丝绳断裂失效分析	4
	某西部油田高温高压气井连续油管断裂原因	4
	某油井油管短节断裂原因分析	4
	弩钩断裂失效分析	4
	起重机钢丝绳断裂失效分析	4
	汽轮机叶片断裂分析	4