316L-16MnR复合板不锈钢侧晶间腐蚀原因分析
REASON ANALYSIS ABOUT INTERGRANULAR CORROSION ON STAINLESS STEEL SIDE OF 316L-16MnR CLADDING PLATE
摘 要
采用GB/T 4334.5-2000标准方法对不锈钢-低合金钢复合板进行晶间腐蚀试验,对不锈钢侧产生裂纹的原因进行了分析。结果表明,由于不锈钢板与低合金钢板的结合面上存在着不可抗拒的碳迁移现象,致使不锈钢板侧过渡区内的奥氏体晶界上聚集着大量的网状碳化物,从而造成晶界上的缺陷,使其在经过硫酸-硫酸铜溶液的腐蚀后,进行弯曲时产生了大量的晶间腐蚀裂纹。
碳迁移现象
晶间腐蚀
网状碳化物
裂纹
Stainless steel and low-alloy steel cladding plate
Carbon transference
Intergranular corrosion
Netty carbide
Crack
Abstract
The cracksin stainless steel and low-alloy steel cladding plate were found after intergranular corrosin examination. The metallographic analysis results showed that,because of the irresistible transference of carbon in binding face between stainless steel plate and low-alloy steel plate,there were lots of netty carbide gathering in the austenitic grain boundary of transitional region of stainless steel plate,which caused the defect in boundary. After eroding in H2SO4-CuSO4 solution and then bending,it appeared lots of intergranular corrosion cracks.
中图分类号 TB331
所属栏目 质量控制与失效分析
基金项目
收稿日期 2007/6/14
修改稿日期
网络出版日期
作者单位点击查看
备注唐翠华(1956-),女,工程师。
引用该论文: TANG Cui-hua,HOU Liang-li. REASON ANALYSIS ABOUT INTERGRANULAR CORROSION ON STAINLESS STEEL SIDE OF 316L-16MnR CLADDING PLATE[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2008, 44(1): 48～50
唐翠华,侯良立. 316L-16MnR复合板不锈钢侧晶间腐蚀原因分析[J]. 理化检验－物理分册, 2008, 44(1): 48～50
被引情况:
【1】刘会云,何 毅,张心金,李 晓, "不锈钢复合板复层晶间腐蚀试验方法和标准",理化检验－物理分册 52, 614-617(2016)
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】李炯辉.金相图谱［M］.北京:机械工业出版社,2006:936．
【2】中国机械工程学会焊接学会.焊接手册［M］.北京:机械工业出版社,1662:597．
【2】中国机械工程学会焊接学会.焊接手册［M］.北京:机械工业出版社,1662:597．
相关信息