空调螺钉热处理工艺的特点

空调螺钉热处理工艺的特点

HEAT TREATMENT PROCESS CHARACTERISTIC ON AIR-CONDITION SCREW

董加坤

摘要

空调螺钉采用在真空条件下高温淬火+低温回火工艺(淬火温度为1 050 ℃,回火温度为200 ℃),淬火介质为高压压缩空气。对热处理后的螺钉进行显微组织观察和分析,并结合该螺钉的材质分析结果,说明该螺钉采用的热处理工艺能使其获得平衡态组织,达到了产品塑性、韧性和耐腐蚀性的最佳配合要求。

标签空调

螺钉

热处理

Air-condition

Screw

Heat treatment

Abstract

The air condition screws were heat-treated in vacuum furnace,in which the quenching temperature was 1 050 ℃ and the tempering temperature was 200 ℃,and the quenching medium was compressive air. The microstructure of screws was observed and analyzed. The results showed that,the processing prompt screw to form the balance microstructure,and finally obtained optimized plastic,toughness and corrosion resistance.

中图分类号 TM201.3

所属栏目试验与研究

基金项目

收稿日期 2006/8/22

修改稿日期

网络出版日期

作者单位点击查看

备注董加坤(1966-),男,工程师,学士。

引用该论文: DONG Jia-kun. HEAT TREATMENT PROCESS CHARACTERISTIC ON AIR-CONDITION SCREW[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2008, 44(3): 123～125
董加坤. 空调螺钉热处理工艺的特点[J]. 理化检验－物理分册, 2008, 44(3): 123～125

论文评价

共有人对该论文发表了看法，其中：

人认为该论文很差

人认为该论文较差

人认为该论文一般

人认为该论文较好

人认为该论文很好

分享论文

参考文献

【1】GB/T 1220-1992 不锈钢棒［S］．

【2】ASTM F899-02 外科器械不锈钢标准规范［S］．

【3】上海市机械制造工艺研究所.金相分析技术［M］.上海:上海科学技术文献出版社,1987．

【4】陈德和.不锈钢及其热处理［M］.北京:机械工业出版社,1973．

相关信息

	标题	相关频次
	17-4PH不锈钢磁粉检测中出现的问题分析	2
	18CrNiMo7-6A钢减速机输出轴断裂原因	2
	20Cr2Ni4钢制打击罩硬度异常分析	2
	304不锈钢薄壁焊管表面残余拉应力的测定及消除	2
	35钢螺钉断裂分析	2
	42CrMo钢齿轮轴断裂原因分析	2
	42CrMo钢蜗杆开裂原因分析	2
	45钢棒料冲击功偏低的原因分析	2
	50Mn钢齿圈断齿原因分析	2
	6.8级冷镦螺栓的表层残余应力分布	2
	65Mn钢锁片断裂分析	2
	65Mn钢锥形垫圈断裂原因	2
	7075铝合金高锁螺母开裂原因	2
	960MPa级含钼低碳钢钼含量与热处理工艺的确定	2
	9Cr2Mo钢转向辊调质开裂原因分析	2
	GH4169合金冷拔管加工工艺参数的优化	2
	GH648合金的热处理适应性	2
	Hollo-Bolt单向螺栓套管肢断裂原因分析	2
	Mg-Al系镁合金的耐蚀性能研究进展	2
	Ni-P化学镀层及其复合镀层结合强度的声发射研究	2
	P22钢的里氏硬度与布氏硬度的转换关系	2
	QBe2铍青铜棒热处理断裂原因分析	2
	SS400热轧碳钢氧化皮的结构改变与保护性	2
	SWRCH15A钢螺钉断裂原因分析	2
	SWRCH22A钢螺钉的断裂原因	2
	SWRCH22A钢自攻螺钉断裂原因分析	2
	SWRCH22A十字头螺钉断裂分析	2
	Ti-6Al-4V合金厚板固溶时效热处理工艺的正交试验优化	2
	ZA40合金热处理工艺的确定	2
	ZG15Cr2Mo1钢力学性能差异较大的原因分析	2