销孔螺栓断裂分析
FRACTURE ANALYSIS OF PIN HOLE BOLT
摘 要
销孔螺栓在服役期限内发生断裂。借助扫描电子显微镜对断口形貌及显微组织进行观察分析。结果表明,由于销孔螺栓的热处理工艺不当,使其显微组织成为珠光体+沿晶界分布的网状铁素体及魏氏体组织,造成晶界弱化,使得销孔螺栓强度降低,在应力的作用下发生疲劳断裂。
热处理工艺
网状铁素体
Pin hole bolt
Heat treatment technology
Network ferrite
Abstract
Pin hole bolt ruptures under its service. Observe and analyze rupture appearance and microstructure by means of SEM. The result shows that improper heat treatment technics causes the microstructure of the pin hole bolt being made of pearlite and network ferrite with ,making the grain boundary serious weakness. The pin hole bolt happens fatigue crack because of stress concentration and its lower strength.
中图分类号 TG76
所属栏目 质量控制与失效分析
基金项目
收稿日期 2007/1/3
修改稿日期
网络出版日期
作者单位点击查看
备注郭全英(1965-),女,高级工程师,硕士。
引用该论文: GUO Quan-ying,CAI Shu-fang,XU Shu-zhen. FRACTURE ANALYSIS OF PIN HOLE BOLT[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2008, 44(4): 209～211
郭全英,蔡淑芳,许淑珍. 销孔螺栓断裂分析[J]. 理化检验－物理分册, 2008, 44(4): 209～211
被引情况:
【1】郭全英,张国玉,孙晶, "卡盘T型块断裂原因分析",理化检验－物理分册 52, 332-334(2016)
【2】蒋立冬,陈营利,朱振荣, "某船用减速器螺栓断口的SEM分析",理化检验－物理分册 45, 351-354(2009)
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】邵奎祥.地角螺栓断裂失效分析［J］.理化检验-物理分册,2004,40(1):37-39．
【2】刘泽坤.40Cr钢螺栓断裂失效分析［J］.理化检验-物理分册,2003,39(1):160-161．
【3】吴 伟.30CrMnSiA钢螺钉断裂失效分析［J］.理化检验-物理分册,2006,42(1):43-44．
【4】杨 力.超高强螺栓断裂失效分析［J］.理化检验-物理分册,2004,40(4):195-198．
【5】安运铮.热处理工艺学［M］.北京:机械工业出版社,1985．
【2】刘泽坤.40Cr钢螺栓断裂失效分析［J］.理化检验-物理分册,2003,39(1):160-161．
【3】吴 伟.30CrMnSiA钢螺钉断裂失效分析［J］.理化检验-物理分册,2006,42(1):43-44．
【4】杨 力.超高强螺栓断裂失效分析［J］.理化检验-物理分册,2004,40(4):195-198．
【5】安运铮.热处理工艺学［M］.北京:机械工业出版社,1985．
相关信息