ELECTROCHEMICAL BEHAVIORS OF CO2 CORROSION ON N80 STEEL AND 09Cr2AlMoRE STEEL
摘 要
利用交流阻抗技术对比研究了N80油套管钢和09Cr2AlMoRE钢(称新型合金)在饱和CO2的地层水中的腐蚀电化学行为,同时利用SEM观察了两种材料在1 MPa,120 ℃腐蚀7 d(天)所成膜的形貌。结果表明,N80钢的阳极电化学阻抗谱出现了高频的容抗弧、中低频的感抗弧和低频的容抗弧;而新型合金的阳极电化学阻抗谱只出现了高、低频容抗弧,感抗弧已很少了。对于阴极电化学阻抗谱,N80钢的阻抗谱只由一容抗弧组成,而新型合金则由高频容抗弧、中频Warburg阻抗和低频容抗弧共同组成。对两种材料阴、阳极过程中极化电阻的计算表明,新型合金阴、阳极过程中的极化电阻大于N80钢相应过程的极化电阻,表明新型合金能有效地抑制了CO2腐蚀。
Abstract
The electrochemical behaviors of N80 steel and 09Cr2AlMoRE steel in stratum water with saturated CO2 were comparably investigated using electrochemical impedance spectra (EIS),and the microstructures of corrosion scales formed on two samples at 1 MPa,120 ℃ for 7 days were also observed by SEM. The results showed that the anodic impedance of N80 steel was consisted of capacitance at high frequency,inductance at middle frequency and capacitance at low frequency. While for the anodic impedance of novel alloy,the spectra was only consisted of capacitance at high and low frequencies,and the inductance shrinked. For the cathodic impedance spectras of two samples,the spectra of N80 steel was only consisted of one capacitance,and the spectra of novel alloy were consisted of capacitance at high frequency,Warburg impedance at middle frequency and capacitance at low frequency. Calculating the polarization impedances of anodic and cathodic processes for two samples,it revealed that the polarization impedances of anodic and cathodic processes for novel alloy were all higher than that for N80 steel,this means that the novel alloy can effectively inhibited the occurrence of CO2 corrosion formed on it.
中图分类号 TG172.3
所属栏目 试验与研究
基金项目
收稿日期 2007/3/9
修改稿日期
网络出版日期
作者单位点击查看
备注翟 文(1980-),女,硕士研究生。
引用该论文: ZHAI Wen,ZHENG Mao-sheng. ELECTROCHEMICAL BEHAVIORS OF CO2 CORROSION ON N80 STEEL AND 09Cr2AlMoRE STEEL[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2008, 44(5): 226~230
翟 文,郑茂盛. 09Cr2AlMoRE钢和N80油套管钢的CO2腐蚀电化学行为[J]. 理化检验-物理分册, 2008, 44(5): 226~230
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】束润涛.12Cr2AlMoV管材、设备及其创新材料-09Cr2AlMoRE[J].石油化工腐蚀与防护,2000,17(1):24-27.
【2】束润涛.耐硫化氢腐蚀的新材料07/09Cr2AlMoRE[J].石油机械,2003,31(4):1-3.
【3】Waard D C,Milliams D E. Carbonic Acid Corrosion of Steel[J]. Corrosion,1975,31(5):177-181.
【4】Ogundele G I,White W E. Some Observations on Corrosion of Carbon Steel in Aqueous Environment Containing Carbon Dioxide[J]. Corrosion,1986,42(2):71-78.
【5】Nesic S,Postlethwaite J,Olsen S. An Electrochemical Model for Prediction of Corrosion of Mild Steel in Aqueous Carbon Dioxide Solutions[J]. Corrosion,1996,52(4):280-294.
【6】Ogundele G I,White W E. Some Observation on Corrosion of Carbon Steel in Aqueous Environments Containing Carbon Dioxide[J]. Corrosion,1986,42(2):71.
【7】陈长风,路民旭,赵国仙,等.N80油套管钢CO2腐蚀阴极过程交流阻抗分析[J].金属学报,2003,39(1):94-98.
【2】束润涛.耐硫化氢腐蚀的新材料07/09Cr2AlMoRE[J].石油机械,2003,31(4):1-3.
【3】Waard D C,Milliams D E. Carbonic Acid Corrosion of Steel[J]. Corrosion,1975,31(5):177-181.
【4】Ogundele G I,White W E. Some Observations on Corrosion of Carbon Steel in Aqueous Environment Containing Carbon Dioxide[J]. Corrosion,1986,42(2):71-78.
【5】Nesic S,Postlethwaite J,Olsen S. An Electrochemical Model for Prediction of Corrosion of Mild Steel in Aqueous Carbon Dioxide Solutions[J]. Corrosion,1996,52(4):280-294.
【6】Ogundele G I,White W E. Some Observation on Corrosion of Carbon Steel in Aqueous Environments Containing Carbon Dioxide[J]. Corrosion,1986,42(2):71.
【7】陈长风,路民旭,赵国仙,等.N80油套管钢CO2腐蚀阴极过程交流阻抗分析[J].金属学报,2003,39(1):94-98.
相关信息