2.25Cr1Mo钢中的夹杂物和晶粒度
INCLUSION AND GRAIN SIZE OF 2.25Cr1Mo STEEL
摘 要
对采用2.25Cr1Mo钢制成的螺纹承压环、封头、接管和法兰上截取的试样进行晶粒度等级评定及夹杂物形态和分布的研究。研究表明,封头和接管处晶粒度等级较高,四个部位试样的晶粒度等级均满足要求,夹杂物以细小的氧化物为主,有少量的硫化物,无硅酸盐类夹杂物,并且夹杂物呈独立分布。
晶粒度
夹杂物
形态分布
2.25Cr1Mo steel
Grain size
Inclusion
Shape distribution
Abstract
The test sample were intercepted from thread bearing circle,end plate,connecter and flange of equipment in order to assessment grain size and shape of inclusion. The grain size was higher in flange and connector,but grain size of four positions satisfied criteria,there were small oxide inclusion and little sulfide,the inclusion distributed independently.
中图分类号 TG111
所属栏目 试验与研究
基金项目
收稿日期 2007/5/31
修改稿日期
网络出版日期
作者单位点击查看
备注秦 华(1978-),女,助教,硕士。
引用该论文: QIN Hua,LIU Li-fang,HU Chuan-shun,TANG Ying-chun,CUI Yong. INCLUSION AND GRAIN SIZE OF 2.25Cr1Mo STEEL[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2008, 44(5): 235～237
秦 华,刘丽芳,胡传顺,唐迎春,崔 勇. 2.25Cr1Mo钢中的夹杂物和晶粒度[J]. 理化检验－物理分册, 2008, 44(5): 235～237
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】李贵军,王乐勤.2.25Cr1Mo钢的中温疲劳裂纹扩展行为研究和加氢反应器的安全分析［J］.压力容器,2004,21(7):18-23．
【2】于兆斌.热处理工艺对2.25Cr1Mo钢的组织和力学性能影响［J］.宽厚板,2005,11(5):25-28．
【3】周华庆.60Si2MnRE钢中夹杂物、微观组织和本质晶粒度的研究［J］.长沙电力学院学报,2001,16(2):77-81．
【4】范海东,翁绍华.35MnVNbTi钢的微合金化与晶粒度的关系［J］.理化检验-物理分册,2004,40(10):490-494．
【5】朱进民.钢中非金属夹杂物对性能的影响［J］.电气牵引,2004,11(2):55-56．
【6】张爱梅.非金属夹杂物对钢的性能的影响［J］.物理测试,2006,24(4):42-45．
【2】于兆斌.热处理工艺对2.25Cr1Mo钢的组织和力学性能影响［J］.宽厚板,2005,11(5):25-28．
【3】周华庆.60Si2MnRE钢中夹杂物、微观组织和本质晶粒度的研究［J］.长沙电力学院学报,2001,16(2):77-81．
【4】范海东,翁绍华.35MnVNbTi钢的微合金化与晶粒度的关系［J］.理化检验-物理分册,2004,40(10):490-494．
【5】朱进民.钢中非金属夹杂物对性能的影响［J］.电气牵引,2004,11(2):55-56．
【6】张爱梅.非金属夹杂物对钢的性能的影响［J］.物理测试,2006,24(4):42-45．
相关信息