小型锅炉锅筒开裂原因分析
CRACKING ANALYSIS OF SMALL SIZED BOILER CANISTER
摘 要
采用化学成分分析,宏、微观组织检验,断口观察和腐蚀产物分析等方法对SUS304奥氏体不锈钢锅炉的锅筒开裂进行了分析。结果表明,环境中存在硫和氯等元素,造成在锅筒板与顶盖的焊接处发生腐蚀而形成腐蚀坑并萌生裂纹,在各种应力作用下裂纹不断扩展,最终导致开裂。
应力腐蚀开裂
锅炉
Austenitic stainless steel
Stress corrosion cracking
Boiler
Abstract
Through analysis of cracking causes in boiler canister of SUS304 (0Cr18Ni9) austenitic stainless steels,the reason for its inactivation was pointed out. After self-coiling welding boiler canister and cover were welded,at the self-coiling stress of boiler canister and welding stress of boiler canister and cover,the self-coiling welding boiler canister appeared stress corrosion cracking at the pitting corrosion by chloride inducement and sulfide accelerating.
中图分类号 TK229.5+1
所属栏目 质量控制与失效分析
基金项目
收稿日期 2007/3/23
修改稿日期
网络出版日期
作者单位点击查看
备注郭海霞(1981-),女,助工。
引用该论文: GUO Hai-xia,YUE Can-fu,YANG Zhi-yong. CRACKING ANALYSIS OF SMALL SIZED BOILER CANISTER[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2008, 44(5): 255～257
郭海霞,岳灿甫,杨之勇. 小型锅炉锅筒开裂原因分析[J]. 理化检验－物理分册, 2008, 44(5): 255～257
被引情况:
【1】李小东,郝习云,陈进,孙晓明, "外压型不锈钢波纹管膨胀节开裂分析",理化检验－物理分册 47, 187-188(2011)
【2】韩波,陈申芳,黄嘉乐, "汽车定子盘开裂原因分析",理化检验－物理分册 47, 189-191(2011)
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】美国金属学会.金属手册 第十卷 失效分析与防护［M］.第八版. 北京:机械工业出版社,1974: 295-297,308-314,828．
相关信息