INFLUENCE FACTORS ON CRANKSHAFT QUALITY OF NODULAR CAST IRON
摘 要
通过对失效的球墨铸铁曲轴的分析和统计,认为造成球铁曲轴断裂失效的主要因素有铸态下存在孔洞类缺陷、等温淬火态时组织脆性较大和正火态时圆角不强化,而曲轴磨损失效的主要因素是润滑不足。提高等温淬火组织的韧性和强化曲轴圆角是防止曲轴断裂失效的主要措施。
Abstract
By failure analysis on crankshaft made of nodular cast iron,depending on the statistics and combining with the actual site condition,it is believed that increasing the toughness of material and intensifying fillet radius are the major measures to prevent from failure of crankshaft. The fillet radius is made by means of rotary rolling,which is an effective process. Improvement of hot process-graining graphite in cast and optimizing isothermal hardening in heat treatment can be mainly adopted.
中图分类号 TG255
所属栏目 质量控制与失效分析
基金项目
收稿日期 2007/11/14
修改稿日期
网络出版日期
作者单位点击查看
备注韩志良(1965-),男,高级工程师,副教授,工学学士。
引用该论文: HAN Zhi-liang,DING Yan-jun,MA Hong-wei. INFLUENCE FACTORS ON CRANKSHAFT QUALITY OF NODULAR CAST IRON[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2008, 44(5): 269~274
韩志良,丁燕君,马红卫. 影响球墨铸铁曲轴质量的因素[J]. 理化检验-物理分册, 2008, 44(5): 269~274
被引情况:
【1】孙浩, "空压机曲轴断裂失效分析",理化检验-物理分册 51, 449-451(2015)
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】[德国]冯·弗里德里希·卡尔·瑙曼,著.机械零件和钢铁材料事故例集[M].陈祝同,蔡德洪,王加英,等,译. 北京:机械工业出版社,1987.
【2】刘佑平.化学成分与孕育方法对球铁曲轴缩松缺陷的影响[J].柴油机·Diesel Engine,2003(2): 40-42.
【3】上海市机械制造工艺研究所.金相分析技术[M].上海:上海科学技术文献出版社,1987.
【4】周旭东.曲轴圆角滚压强化技术综述史效强[J].内燃机配件,2005(6): 26-29.
【5】程绍桐.氮化+圆角滚压复合强化球墨铸铁曲轴的应用研究[J].内燃机配件,2006(1): 8-11.
【6】北京铸造学会. 铸件质量手册[M].北京:机械工业出版社,1988.
【7】韩志良.磨损曲轴失效分析[J].国内外金属热处理,2001(4): 6-8.
【2】刘佑平.化学成分与孕育方法对球铁曲轴缩松缺陷的影响[J].柴油机·Diesel Engine,2003(2): 40-42.
【3】上海市机械制造工艺研究所.金相分析技术[M].上海:上海科学技术文献出版社,1987.
【4】周旭东.曲轴圆角滚压强化技术综述史效强[J].内燃机配件,2005(6): 26-29.
【5】程绍桐.氮化+圆角滚压复合强化球墨铸铁曲轴的应用研究[J].内燃机配件,2006(1): 8-11.
【6】北京铸造学会. 铸件质量手册[M].北京:机械工业出版社,1988.
【7】韩志良.磨损曲轴失效分析[J].国内外金属热处理,2001(4): 6-8.
相关信息