EFFECT OF COOLING CONDITIONS ON THE MICROSTRUCTURE AND MECHANICAL PROPERTIES OF ULTRAFINE GRAINED STEEL IN WELDED JOINTS
摘 要
400 MPa级超级钢主要特征是高洁净度和超细晶粒组织。采用钨极氩弧焊对400 MPa级超级钢施焊,并对其空冷和水冷两种冷却方式下的显微组织和力学性能进行分析。结果表明,空冷条件下焊接接头热影响区(HAZ)晶粒严重长大、强度下降,并出现软化区;焊接过程采用喷水冷却加快了冷却速度,有效抑制了焊接接头热影响区晶粒的长大,改善了接头组织,提高了贝氏体和低碳马氏体的含量,进而改善了接头的综合力学性能,满足实际焊接要求。
Abstract
The 400 MPa grade ultra-fine grained steel is characterized by its higher cleanness and ultra-fine grain. The 400 MPa grade ultra-fine grained steel were welded by tungsten argon shielded arc welding,the microstructure and mechanical properties of welded joints under different cooling conditions of air cooling and water cooling were analyzed. The results show that the cases about grain size increasing greatly,strength decreasing and softening area appears do exist in HAZ of welded joints of 400 MPa grade ultrafine grained steel. Using spraying water to speed up the cooling rate in the welding process,could suppress the cases about grain size increasing in HAZ of welded joints effectively,improve the microstructure compositions,and enhance the contents of bainite and low-carbon martensite,then improve the comprehensive mechanics performance of the welded joint,so it could satisfy the actual operation requirements.
中图分类号 TG142.1
所属栏目 试验与研究
基金项目
收稿日期 2007/7/23
修改稿日期
网络出版日期
作者单位点击查看
备注徐春华(1983-),男,硕士研究生。
引用该论文: XU Chun-hua,ZHAO Hong-yun,YANG Xian-qun,WU Jian-qian. EFFECT OF COOLING CONDITIONS ON THE MICROSTRUCTURE AND MECHANICAL PROPERTIES OF ULTRAFINE GRAINED STEEL IN WELDED JOINTS[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2008, 44(7): 342~345
徐春华,赵洪运,杨贤群,吴剑谦. 冷却条件对超级钢焊接接头组织和性能的影响[J]. 理化检验-物理分册, 2008, 44(7): 342~345
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】王 成. 400 MPa级超级钢激光焊接及其焊接性研究[D]. 北京:清华大学,2002.
【2】彭 云,田志凌,何长红,等. 400 MPa级超细晶粒钢板焊接热影响区的组织和力学性能[J]. 焊接学报,2003(5): 21-24.
【3】赵洪运,王国栋,刘相华,等. 再加热温度对400 MPa级超级钢组织和性能的影响[J]. 金属热处理,2005,30(2): 40-43.
【4】赵洪运,王国栋,杨德惠,等. 喷水冷却对400 MPa级超细晶粒钢焊接接头组织和性能的影响[J]. 金属热处理,2005,30(11): 28-30.
【5】安 民,孙祖庆. 低碳钢奥氏体晶粒控制对应变强化的影响[J]. 金属学报,2000,36(10): 1055-1060.
【2】彭 云,田志凌,何长红,等. 400 MPa级超细晶粒钢板焊接热影响区的组织和力学性能[J]. 焊接学报,2003(5): 21-24.
【3】赵洪运,王国栋,刘相华,等. 再加热温度对400 MPa级超级钢组织和性能的影响[J]. 金属热处理,2005,30(2): 40-43.
【4】赵洪运,王国栋,杨德惠,等. 喷水冷却对400 MPa级超细晶粒钢焊接接头组织和性能的影响[J]. 金属热处理,2005,30(11): 28-30.
【5】安 民,孙祖庆. 低碳钢奥氏体晶粒控制对应变强化的影响[J]. 金属学报,2000,36(10): 1055-1060.
相关信息