高强度钛合金螺栓断裂失效分析
FRACTURE ANALYSIS OF THE TITANIUM ALLOY BOLT WITH HIGH STRENGTH
摘 要
规格为M4×30 mm高强度钛合金螺栓在正常预紧装配后自行断裂。采用金相检验、扫描电镜断口分析、二次离子质谱分析和螺栓的受力分析等方法对螺栓断裂的原因进行了分析。结果表明,螺栓断裂的性质为低应力脆性断裂,断裂机理为氢致延迟断裂,导致螺栓氢致延迟断裂的原因主要与该批棒材原始氢含量过高有关。
螺栓
氢脆
失效分析
Titanium alloy
Bolt
Hydrogen embrittlement
Failure analysis
Abstract
Failure occured when the high strength titanium alloy bolt of M4×30 mm being tightened during assembly. The failure was analyzed by means of metallographic testing,SEM,SIMS,and bolt stress analysis,and the results showed that was a low stress brittle fracture. The fracture mechanism was hydrogen induced delay fracture due to the high content of hydrogen in the bar material.
中图分类号 TG146.2+3
所属栏目 质量控制与失效分析
基金项目
收稿日期 2007/3/1
修改稿日期
网络出版日期
作者单位点击查看
备注朱铭德(1956-),男,高级工程师,学士。
引用该论文: ZHU Ming-de,SHEN Yi-nuo. FRACTURE ANALYSIS OF THE TITANIUM ALLOY BOLT WITH HIGH STRENGTH[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2008, 44(8): 446～450
朱铭德,沈一诺. 高强度钛合金螺栓断裂失效分析[J]. 理化检验－物理分册, 2008, 44(8): 446～450
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】吴连生,刘正义,张静江,等.机械装备失效分析图谱［M］.广州:广东科技出版社,1990:273-275．
【2】美国金属学会.金属手册 第十卷 失效分析与预防［M］.北京:机械工业出版社,1975:334．
【3】万晓景.金属的氢脆［J］.材料保护,1979(3):11-25．
【4】王永庆.30CrMnSiNi2A螺栓断裂分析［J］.理化检验-物理分册,2000,36(10):461-463．
【2】美国金属学会.金属手册 第十卷 失效分析与预防［M］.北京:机械工业出版社,1975:334．
【3】万晓景.金属的氢脆［J］.材料保护,1979(3):11-25．
【4】王永庆.30CrMnSiNi2A螺栓断裂分析［J］.理化检验-物理分册,2000,36(10):461-463．
相关信息