蒸汽管线三通管的泄漏原因分析
LEAKAGE ANALYSIS OF THREE-WAY TUBE ON STEAM PIPELINE
摘 要
催化装置的蒸汽管线上有多个三通管均在焊缝处发生蒸汽泄漏。采用化学成分分析、硬度测试、宏观和微观分析等方法对泄漏的三通管进行了分析。结果表明,由于在焊接时,接口处未焊透留下了缝隙,在工作介质和焊接应力的长期作用下产生了缝隙腐蚀和应力腐蚀,最终导致泄漏。
焊缝
未焊透
缝隙腐蚀
应力腐蚀
Three-way tube
welding line
spilly place
gap corrosion
stress corrosion
Abstract
The steam leakage of the three-way tubes on the steam pipeline of a catalytic device happened in the welding line.The leakage analysis was made by means of chemical composition,hardness,macrostructure and microstructure examination etc.The results showed that the gap corrosion and stress corrosion was occurred at the welding line of the three-way tubes in long-term corrosion environments,by no welding on gaps caused during welding.
中图分类号 TE986
所属栏目 质量控制与失效分析
基金项目
收稿日期 2008/8/10
修改稿日期
网络出版日期
作者单位点击查看
备注谷志刚(1954-),男,高级工程师,学士。
引用该论文: GU Zhi-gang,YOU Xiang-qun,LI Wei-hang. LEAKAGE ANALYSIS OF THREE-WAY TUBE ON STEAM PIPELINE[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2008, 44(9): 501～503
谷志刚,由向群,李伟航. 蒸汽管线三通管的泄漏原因分析[J]. 理化检验－物理分册, 2008, 44(9): 501～503
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】GB/T 699-1999 优质碳素结构钢[S]．
【2】姚红宇. 腐蚀环境作用下失效的失效分析[J]. 理化检验-物理分册,2005,41(11)：590．
【3】赵麦群,雷阿丽. 金属的腐蚀与防护[M]. 北京：国防工业出版社,2002．
【2】姚红宇. 腐蚀环境作用下失效的失效分析[J]. 理化检验-物理分册,2005,41(11)：590．
【3】赵麦群,雷阿丽. 金属的腐蚀与防护[M]. 北京：国防工业出版社,2002．
相关信息