304不锈钢低温分离器开裂原因分析
CRACKING ANALYSIS OF SEPARATOR MADE OF 304 STAINLESS STEEL
摘 要
采用残余应力检测、常规力学性能试验以及金相分析等方法对304不锈钢低温分离器的封头开裂原因进行分析。结果表明,开裂是由应力腐蚀引起的;其原因是工作介质中有含量较高的硫,而封头-筒体对接环焊缝区域存在的残余应力促使开裂的发生。
失效分析
应力腐蚀开裂
304 stainless steel
failure analysis
stress corrosion cracking
Abstract
The cracking analysis of separator made of 304 stainless steel had been conducted by examining residual stress,testing mechanical performance and analyzing the microstructures. The results showed that the cracking was typical stress corrosion cracking. The cracking was induced by the sulfide in the working medium. The circumferential working stress may play a dominant role and the residual stress due to welding was also responsible for the cracking.
中图分类号 TG142.71
所属栏目 质量控制与失效分析
基金项目 “十一五”国家科技支撑项目(2006BKA02B02)
收稿日期 2007/11/27
修改稿日期
网络出版日期
作者单位点击查看
备注丁大伟(1981-),男,硕士研究生。
引用该论文: DING Da-wei,XU Xue-dong,GU Bao-lan,LIU Jin-yan,ZHANG Yi-liang. CRACKING ANALYSIS OF SEPARATOR MADE OF 304 STAINLESS STEEL[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2008, 44(10): 564～566
丁大伟,徐学东,顾宝兰,刘金燕,张亦良. 304不锈钢低温分离器开裂原因分析[J]. 理化检验－物理分册, 2008, 44(10): 564～566
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】王晓敏. 工程材料学[M]. 北京: 机械工业出版社,1999: 150．
【2】任 颂. 钢铁金相图谱[M]. 上海:上海科技文献出版社,2003: 368．
【3】王正樵,于幼林. 不锈钢[M]. 北京: 化学工业出版社,1991: 109．
【4】冈毅民. 不锈钢腐蚀手册[M]. 北京: 冶金工业出版社,1982: 228．
【5】孙 智,江 利,应鹏展. 失效分析——基础与应用[M]. 北京: 机械工业出版社,2005: 128．
【2】任 颂. 钢铁金相图谱[M]. 上海:上海科技文献出版社,2003: 368．
【3】王正樵,于幼林. 不锈钢[M]. 北京: 化学工业出版社,1991: 109．
【4】冈毅民. 不锈钢腐蚀手册[M]. 北京: 冶金工业出版社,1982: 228．
【5】孙 智,江 利,应鹏展. 失效分析——基础与应用[M]. 北京: 机械工业出版社,2005: 128．
相关信息