TP2铜管退火后起皮原因分析
BLISTER CAUSE ANALYSIS OF TP2 COPPER TUBE AFTER ANNEALING
摘 要
采用化学成分分析、金相检验、扫描电镜和能谱仪分析等方法对TP2铜铸锭及其挤制管坯起皮的原因进行了分析。结果表明,在TP2铜铸锭和挤制管坯均分布着Cu2O颗粒。当挤制管在还原性气氛下退火时,因还原反应产生的气体而造成管坯表面起皮。采取了相应措施解决了起皮问题。
起皮
颗粒
退火
TP2 copper tube
bubble
granule
annealing
Abstract
Blister appeared on the surface of TP2 copper tube and the casting was studied by means of optical microscopy and SEM and EDS instrument. The results showed that Cu2O granules existed in TP2 copper cast ingot and extruding tube. During anneal processing in the reductive atmosphere, the air came from reductive reaction letted out to form bubbles on the tube surface.The measures to reduce the blister were discussed.
中图分类号 TG146.1+1
所属栏目 实践经验
基金项目
收稿日期 2007/8/7
修改稿日期
网络出版日期
作者单位点击查看
备注杨 忠(1968-),男,工程师。
引用该论文: YANG Zhong. BLISTER CAUSE ANALYSIS OF TP2 COPPER TUBE AFTER ANNEALING[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2008, 44(11): 661～663
杨 忠. TP2铜管退火后起皮原因分析[J]. 理化检验－物理分册, 2008, 44(11): 661～663
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】张 劭. 关于紫铜熔铸中吸气的原因及其危害[J]. 特种铸造及有色合金,1998,5: 42-44．
【2】郑子樵. 材料科学基础［M］. 长沙: 中南大学出版社,2005: 381．
【2】郑子樵. 材料科学基础［M］. 长沙: 中南大学出版社,2005: 381．
相关信息