带涂层焊缝的电磁涡流检测
Electromagnetic Eddy Current Inspection for Coated Welded Lines
摘 要
采用电磁涡流法对16MnR钢焊缝试件进行了涡流检测。得出在焊缝表面较平整情况下, 检测裂纹的能力同涂层厚度间的定性关系。渗透检测对比结果表明, 电磁涡流法在表面涂层平均厚度不大于500 μm时, 可检出各种形式焊缝表面的裂纹、气孔和咬边等缺陷。
焊缝
涂层
裂纹
Electromagnetism Eddy current
Welded lines
Coat
Crack
Abstract
16MnR steel welded lines are tested with electromagnetic eddy current. The relation of the ability of crack testing and the coat thickness in an exteriorly clean weld was deduced. By the comparison with the penetrante test result, it shows that this measure can test diversified exterior flaws, such as cracks, pore and gnawing and so on, when the cote thickness is less than 500 μm.
中图分类号 TG115.28
所属栏目 仪器方法
基金项目
收稿日期 2010/3/25
修改稿日期
网络出版日期
作者单位点击查看
备注吕香慧(1977-), 女, 工程师, 主要从事无损检测方面的工作。
引用该论文: LV Xiang-Hui,ZHANG Yu,LOU Miao,HU Xin-Dong. Electromagnetic Eddy Current Inspection for Coated Welded Lines[J]. Nondestructive Testing, 2010, 32(6): 441～443
吕香慧,张 宇,楼 淼,胡新东. 带涂层焊缝的电磁涡流检测[J]. 无损检测, 2010, 32(6): 441～443
被引情况:
【1】姚力,巩德兴,马学荣,乐开白,左继锋, "承压设备的电磁检测新技术检验",无损检测 34, 28-31(2012)
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】徐可北, 周俊华, 等.涡流检测[M].北京: 机械工业出版社, 2004.
【2】林俊明, 张开良, 林发炳, 等.焊缝表面裂纹涡流检测技术[J].中国锅炉压力容器安全, 2005, 20(6): 33-36.
【3】刘凯, 沈功田.带防腐层焊缝疲劳裂纹的快速探伤[J].中国锅炉压力容器安全, 2004, 20(6): 29-32.
【4】JB/T 10658—2006 基于复平面分析的焊缝涡流检测[S].
【2】林俊明, 张开良, 林发炳, 等.焊缝表面裂纹涡流检测技术[J].中国锅炉压力容器安全, 2005, 20(6): 33-36.
【3】刘凯, 沈功田.带防腐层焊缝疲劳裂纹的快速探伤[J].中国锅炉压力容器安全, 2004, 20(6): 29-32.
【4】JB/T 10658—2006 基于复平面分析的焊缝涡流检测[S].
相关信息