红外光谱法分析二元聚合物
INFRARED SPECTROMETRIC ANALYSIS OF BINARY POLYMER
摘 要
在偶氮二异丁腈(AIBN)引发下,苯乙烯和丙烯腈的自由基发生聚合而产生苯乙烯-丙烯腈二元聚合物,制取了一系列丙烯腈不同含量的聚合物.选取705 cm-1和2 240 cm-1两个红外吸收峰分别测定苯乙烯和丙烯腈.苯乙烯吸光度与丙烯腈吸光度之比值和聚合物中丙烯腈摩尔分数的倒数呈线性关系,由这些数据回归建立工作曲线.
分析
自由基聚合
回归分析
IR spectroscopy
Analysis
Free radical polymerization
Regression analysis
Abstract
Binary polymer styrene-acrylonitrile was prepared by polymerization of styrene and acrylonitrile free radicals induced by azobisisobutyronnitrile (AIBN).A series of binary polymers with different fractions of acrylonitrile was prepared.Two infrared absorption peaks at wave numbers of 705 cm-1 and 2 240 cm-1 were selected for the determination of styrene and acrylonitrile in binary polymers,respectively.Linearity relationship between the ratio of styrene absorbance to the acrylonitrile absorbance with the reciprocal molar fraction of acrylonitrile in the binary polymer was presented.Working curve was established on the basis of regression analysis of the above mentioned data.
中图分类号 O657.33
所属栏目 工作简报
基金项目 安徽省自然科学基金资助(No 03045101)
收稿日期 2005/1/17
修改稿日期
网络出版日期
作者单位点击查看
备注杨捷(1964-),男,安徽繁昌人,副研究员,主要从事材料合成及傅立叶红外光谱的应用研究.
引用该论文: YANG Jie,SONG Ji-mei,CHENG Yan-an. INFRARED SPECTROMETRIC ANALYSIS OF BINARY POLYMER[J]. Physical Testing and Chemical Analysis part B:Chemical Analysis, 2006, 42(10): 818～820
杨捷,宋继梅,程延安. 红外光谱法分析二元聚合物[J]. 理化检验－化学分册, 2006, 42(10): 818～820
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】王喜贵,王文锦.红外光谱自动定量分析[J].内蒙古师大学报,1992,21(2):27-29．
【2】张叔良,易大年,吴天明.红外光谱分析与新技术[M].北京:中国医药科技出版社,1993:185-186．
【3】清华大学分析化学教研室编.现代仪器分析.上册[M].北京:清华大学出版社,1983:212-213．
【4】荆煦瑛.傅立叶变换红外光谱的应用研究[M].吉林:吉林大学出版社,1989:245．
【5】武汉大学主编.分析化学[M].北京:高等教育出版社,2000:232．2007年《分析试验室》征订启事
【2】张叔良,易大年,吴天明.红外光谱分析与新技术[M].北京:中国医药科技出版社,1993:185-186．
【3】清华大学分析化学教研室编.现代仪器分析.上册[M].北京:清华大学出版社,1983:212-213．
【4】荆煦瑛.傅立叶变换红外光谱的应用研究[M].吉林:吉林大学出版社,1989:245．
【5】武汉大学主编.分析化学[M].北京:高等教育出版社,2000:232．2007年《分析试验室》征订启事
相关信息