氧化钛烧结体的氧含量测定
Determination of Oxide Content in Titanium Oxide Sinter
摘 要
用电子探针X射线微分析(EPMA)方法测定了一系列氧化钛烧结体中的氧含量,并用X射线衍射(XRD)分析对其相态作了研究,所得的结果指出根据产品的氧含量与其某些物理特性之间的内在联系,即可从其表观的某些物理性质估计某一烧结产品的氧化物含量,而所得结果对下一步的镀膜工作具有指导意义.
氧化物含量
EPMA
XRD
Titanium oxide
Oxide content
EPMA
XRD
Abstract
The oxide contents of a series of titanium oxide sinter′ were determined by electron probe X-ray micro-analysis (EPMA) and phase analysis of the oxide sinters was studied by X-ray diffraction method (XRD).It was concluded that on the base of relationship of certain physical characteristics of the products with their contents of oxides,it is possible to evaluate the oxide content of a sintered product from certain of its apparent physical character.The results obtained were of guiding meaning for the membrane coating in the next processing.
中图分类号 O657.62
所属栏目 工作简报
基金项目 国家863计划项目(2003AA327040)
收稿日期 2006/12/10
修改稿日期
网络出版日期
作者单位点击查看
备注赵鑫(1980-),男,内蒙古乌海人,硕士研究生,主要研究方向为功能材料.
引用该论文: ZHAO Xin,SHEN Jian-yun,WANG Xing-ming,HUANG Song-tao,CHU Mao-you,GUO Fen,WANG Zan-hai. Determination of Oxide Content in Titanium Oxide Sinter[J]. Physical Testing and Chemical Analysis part B:Chemical Analysis, 2008, 44(2): 119～122
赵鑫,沈剑韵,王星明,黄松涛,储茂友,郭奋,王赞海. 氧化钛烧结体的氧含量测定[J]. 理化检验－化学分册, 2008, 44(2): 119～122
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】钟迪生.真空镀膜-光学材料的选择与应用[M].沈阳:辽宁大学出版社,2001:253-265．
【2】GB/T 15074-1994电子探针定量分析标准方法通则[S]．
【3】毛允静.钢中低碳的电子探针定量分析[J].冶金分析,2003,23(1):59．
【4】尚玉华,徐乐英.用电子探针测定碳的X光光谱[J].电子显微学报,1995,14(3):210．
【5】徐乐英,尚玉华.用电子探针定量分析超轻元素中的几个问题[J].分析测试学报,1994,13(5):37．
【6】毛允静.在EPMA中有关标样问题[J].电子显微学报,1995,14(5):385．
【7】陈世朴,王永瑞.金属电子显微分析[M].北京:机械工业出版社,1982:200．
【8】毛允静,赵向荣.轻元素定量EPMA的通用修正程序[J].电子显微学报,1994,13(2):109．
【9】Bastin G F,Heijligers H J M.超轻元素的电子探针定量分析[J].国外矿床地质,1996,2:10．
【10】Tachibana Y,Ohsaki H.TiO2-x sputter for high rate deposition of TiO2[J]. Vacuum,2000,59:836．
【11】Ohsaki H,Tachibana Y.High rate sputter deposition of TiO2 from TiO2-x target[J].Thin Solid Films,1999,351:57．
【12】Poelman H,Tomaszewski H.Effect of the oxygen deficiency of ceramic TiO2-x targets on the deposition of TiO2 thin films by DC magnetron sputtering[J].Surface and Interface Analysis,2004,36:1167．
【2】GB/T 15074-1994电子探针定量分析标准方法通则[S]．
【3】毛允静.钢中低碳的电子探针定量分析[J].冶金分析,2003,23(1):59．
【4】尚玉华,徐乐英.用电子探针测定碳的X光光谱[J].电子显微学报,1995,14(3):210．
【5】徐乐英,尚玉华.用电子探针定量分析超轻元素中的几个问题[J].分析测试学报,1994,13(5):37．
【6】毛允静.在EPMA中有关标样问题[J].电子显微学报,1995,14(5):385．
【7】陈世朴,王永瑞.金属电子显微分析[M].北京:机械工业出版社,1982:200．
【8】毛允静,赵向荣.轻元素定量EPMA的通用修正程序[J].电子显微学报,1994,13(2):109．
【9】Bastin G F,Heijligers H J M.超轻元素的电子探针定量分析[J].国外矿床地质,1996,2:10．
【10】Tachibana Y,Ohsaki H.TiO2-x sputter for high rate deposition of TiO2[J]. Vacuum,2000,59:836．
【11】Ohsaki H,Tachibana Y.High rate sputter deposition of TiO2 from TiO2-x target[J].Thin Solid Films,1999,351:57．
【12】Poelman H,Tomaszewski H.Effect of the oxygen deficiency of ceramic TiO2-x targets on the deposition of TiO2 thin films by DC magnetron sputtering[J].Surface and Interface Analysis,2004,36:1167．
相关信息