离心浇铸制样-X射线荧光光谱法测定钼铁中钼硅磷铜
XRFS Determination of Molybdenum,Silicon,Phosphorus and Copper in Ferromolybdenum with Samples Prepared by Centrifugal Casting
摘 要
为克服钼铁中元素的偏析,应用了离心浇铸工艺制成蘑菇状的片样供X射线荧光光谱法用,对制样的过程作了详细的叙述.为制作工作曲线用了5个国外内钼铁标准样品及3个内控标准样品,用同一钼铁样品制备6个片样,按试验条件分别进行钼、硅、磷、铜4元素的测定,并对方法的精密度进行了试验,测得相对标准偏差(n=6)在0.24%~5.41%之间.在分析4个钼铁试样时,所得上述4元素的测定值与用化学方法所测得结果一致.
样品制备
离心浇铸
钼铁
XRFS
Sample preparation
Centrifugal casting
Ferromolybdenum
Abstract
To overcome segregation of ferromolybdenum,the technology of centrifugal casting was applied to prepare mushroom shaped piece sample used for XRFS determination of Mo,Si,P and Cu.Details of the sample preparation were given.Five standard samples and 3 working standards were used for preparation of working curves of the elements determined.Precision was tested with 6 piece samples prepared from a same sample and analyzed by the proposed method for the contents of Mo,Si,P and Cu,values of RSD′s (n=6) found were in the range of 0.24%-5.41%.In the analysis of 4 ferromolybdenum samples,the results of the 4 elements found by this method were in consistency with the results obtained by chemical methods.
中图分类号 O657.34
所属栏目 工作简报
基金项目
收稿日期 2009/1/12
修改稿日期
网络出版日期
作者单位点击查看
备注戴学谦(1961-),男,上海人,高级工程师,主要研究方向为仪器分析和标准样品研制技术.
引用该论文: DAI Xue-qian. XRFS Determination of Molybdenum,Silicon,Phosphorus and Copper in Ferromolybdenum with Samples Prepared by Centrifugal Casting[J]. Physical Testing and Chemical Analysis part B:Chemical Analysis, 2009, 45(5): 549～551
戴学谦. 离心浇铸制样-X射线荧光光谱法测定钼铁中钼硅磷铜[J]. 理化检验－化学分册, 2009, 45(5): 549～551
被引情况:
【1】张秀芳,陆晓明, "熔融制样-X射线荧光光谱法测定锰铁中硅、锰、磷、铬、镍和铜",理化检验－化学分册 51, 1110-1112(2015)
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】铁生年,苗瑞雪.钼铁中Mo,Si,Cu的X射线荧光光谱分析[J].冶金分析,1999,19(5):53-54．
【2】陆晓明,金德龙,林国强,等.离心浇铸制样X射线荧光光谱测定铬铁中铬、硅、磷[J].冶金分析,2005,25(1):54-54．
【3】陆晓明,金德龙.离心浇铸制样X射线荧光光谱法测定锰铁中锰硅磷[J].冶金分析,2008,28(9):34-37．
【4】中国机械工程学会,理化检验分会.全国化学与光谱分析会议论文集[C].兰州:中国机械工程学会,理化分会,2008:257-259．
【5】中国金属学会,冶金分析编辑部.中国金属学会冶金分析编辑部.国际冶金及材料分析测试学术报告会论文集[C].北京:中国金属学会,冶金分析编辑部,2008:226-229．
【6】中国金属学会,冶金分析编辑部.中国金属学会第十三届分析测试学术年会论文集[C].北京:中国金属学会,冶金分析编辑部,2006:464-466．
【2】陆晓明,金德龙,林国强,等.离心浇铸制样X射线荧光光谱测定铬铁中铬、硅、磷[J].冶金分析,2005,25(1):54-54．
【3】陆晓明,金德龙.离心浇铸制样X射线荧光光谱法测定锰铁中锰硅磷[J].冶金分析,2008,28(9):34-37．
【4】中国机械工程学会,理化检验分会.全国化学与光谱分析会议论文集[C].兰州:中国机械工程学会,理化分会,2008:257-259．
【5】中国金属学会,冶金分析编辑部.中国金属学会冶金分析编辑部.国际冶金及材料分析测试学术报告会论文集[C].北京:中国金属学会,冶金分析编辑部,2008:226-229．
【6】中国金属学会,冶金分析编辑部.中国金属学会第十三届分析测试学术年会论文集[C].北京:中国金属学会,冶金分析编辑部,2006:464-466．
相关信息