电感耦合等离子体原子发射光谱法快速测定水泥中三氧化硫
ICP-AES Determination of SO3 in Cement
摘 要
水泥样品经硝酸-盐酸(2+6)混合溶液溶解后,采用电感耦合等离子体原子发射光谱法测定水泥中的三氧化硫的含量.在基体中不含有钙元素时,选择波长为180.7 nm谱线的作为测定三氧化硫的分析线;当基体中含有钙元素时,选择波长为182.0 nm的谱线作为分析线.方法的检出限(3s)为20 μg·L-1.该方法用于测定标准物质(GBW 03201a,GBW 03205)中三氧化硫的含量,相对标准偏差(n=10)在1.00%~0.56%之间,所得结果与标准值相一致.
水泥
三氧化硫
ICP-AES
Cement
SO3
Abstract
The cement sample was dissolved with a mixed solution of HNO3-HCl(2+6),and the amount of S in the sample solution was determined by ICP-AES.Wavelength of 180.7 nm was selected as analytical spectral line without the presence of Ca in matrix,and wavelength of 182.0 nm was selected in the presence of Ca.Detection limit (3s) of the method found was 20 μg·L-1.The proposed method was used in the determination of SO3 in 2 standard cement samples (GBW 03201a,GBW 03205),giving values of RSD′s (n=10) of 1.00% and 0.56% respectively.The results obtained were in conformity with standard values.
中图分类号 O657.31
所属栏目 试验与研究
基金项目
收稿日期 2009/3/3
修改稿日期
网络出版日期
作者单位点击查看
备注蒋天成(1966-),男,广西桂林人,工程师,主要从事化学分析测试研究工作.
引用该论文: JIANG Tian-cheng. ICP-AES Determination of SO3 in Cement[J]. Physical Testing and Chemical Analysis part B:Chemical Analysis, 2009, 45(9): 1015～1016
蒋天成. 电感耦合等离子体原子发射光谱法快速测定水泥中三氧化硫[J]. 理化检验－化学分册, 2009, 45(9): 1015～1016
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】邵春山.实用水泥生产控制分析[M].北京:中国建材工业出版社,1999:183．
【2】张伟东,周春丽,李建梅,等.ICP-AES法测定水泥及熟料中三氧化硫[J].理化检验-化学分册,2000,36(4):174,176．
【3】谢华林.ICP-AES法测定水泥中硫的研究[J].水泥工程,2004(3):60-61．
【4】蒋蓉.ICP-AES法快速测定水泥熟料中三氧化硫的含量[J].武汉理工大学学报,2004,26(2):14-16．
【2】张伟东,周春丽,李建梅,等.ICP-AES法测定水泥及熟料中三氧化硫[J].理化检验-化学分册,2000,36(4):174,176．
【3】谢华林.ICP-AES法测定水泥中硫的研究[J].水泥工程,2004(3):60-61．
【4】蒋蓉.ICP-AES法快速测定水泥熟料中三氧化硫的含量[J].武汉理工大学学报,2004,26(2):14-16．
相关信息