High Frequency Furnace Combustion-IR Spectrometric Determination of Carbon and Sulfur in High Nickel Corrosion Resistant Alloys
摘 要
提出了高频炉燃烧-红外吸收光谱法测定高镍耐蚀合金中碳硫的方法,对试验条件进行了优化,选择钨锡混合助熔剂用量为0.6 g,样品称样量为0.5 g,碳的分析时间为35 s,硫的分析时间为60 s.取标准样品(IARM 67B,IARM 69C,IARM 60B)进行准确度和精密度试验,测定结果与认定值相符,碳和硫的相对标准偏差(n=10)分别小于4%和30%.
高镍耐蚀合金
碳
硫
IR spectrometry
High nickel corrosion resistant alloy
Carbon
Sulfur
Abstract
A method for the determination of carbon and sulfur in high nickel corrosion resistant alloys by high frequency furnace combustion-IR spectrometry was proposed. The optimum experimental conditions were found as follow: ① amount of mixed flux of W and Sn: 0.6 g;② amount of sample: 0.5 g;③ analytical time for carbon: 35 s;④ analytical time for sulfur: 60 s. Tests for accuracy and precision were made with standard samples of IARM 67B,IARM 69C and IARM 60B,giving results in consistency with the standard values. Values of RSD′s (n=10) of carbon and sulfur found were less than 4% and 30%,respectively.
中图分类号 O657.33
所属栏目 工作简报
基金项目 中国石油天然气集团公司应用基础研究项目(2008A-3001,2008A-3005)
收稿日期 2010/4/20
修改稿日期
网络出版日期
作者单位点击查看
备注刘养勤(1976-),女,陕西周至人,工程师,硕士,主要从事石油管材化学分析研究与质量技术监督工作.
引用该论文: LIU Yang-qin,SHAO Xiao-dong,QU Lu-lu. High Frequency Furnace Combustion-IR Spectrometric Determination of Carbon and Sulfur in High Nickel Corrosion Resistant Alloys[J]. Physical Testing and Chemical Analysis part B:Chemical Analysis, 2010, 46(8): 895～896
刘养勤,邵晓东,曲璐璐. 高频炉燃烧-红外吸收光谱法测定高镍耐蚀合金中碳硫[J]. 理化检验－化学分册, 2010, 46(8): 895～896
被引情况:
【1】鲁毅,柳洪超,郭国建,吴立军,尤瑜生, "高频感应燃烧-红外吸收光谱法测定碳化硅中总碳含量",理化检验－化学分册 51, 1457-1459(2015)
【2】刘攀,唐伟,张斌彬,李治亚, "高频感应燃烧-红外吸收光谱法在分析金属材料中碳、硫的应用",理化检验－化学分册 52, 109-118(2016)
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】陈长丰,范成武,郑树启,等.高温高压H2S/CO2 G3镍基合金表面的XPS分析[J].中国有色金属学报,2008,18(11):2050-2055．
【2】黄晓斌.G3合金无缝管制管工艺研究[J].特钢技术,2008,14(56):17-20．
【3】佟梅,包耀宗,董瀚,等.高酸性气田用油管材料G3、825合金的高温变形特性[J].机械工程材料,2009,33(2):56-58．
【4】徐增华.金属耐蚀材料[J].腐蚀与防护,2001,22(9):413-416．
【5】邢卓.Hastelloy C系列合金综述[J].化工设备与管道,2007,44(2):51-58．
【6】万军.镍及镍合金的焊接[J].锅炉制造,2004,193(3):32-34．
【7】宋维第,孙莹,陈明.感应燃烧红外吸收法测定镍基高温合金中痕量硫[J].冶金分析,2004,24(8):57-59．
【2】黄晓斌.G3合金无缝管制管工艺研究[J].特钢技术,2008,14(56):17-20．
【3】佟梅,包耀宗,董瀚,等.高酸性气田用油管材料G3、825合金的高温变形特性[J].机械工程材料,2009,33(2):56-58．
【4】徐增华.金属耐蚀材料[J].腐蚀与防护,2001,22(9):413-416．
【5】邢卓.Hastelloy C系列合金综述[J].化工设备与管道,2007,44(2):51-58．
【6】万军.镍及镍合金的焊接[J].锅炉制造,2004,193(3):32-34．
【7】宋维第,孙莹,陈明.感应燃烧红外吸收法测定镍基高温合金中痕量硫[J].冶金分析,2004,24(8):57-59．
相关信息