Effects of Alternating Magnetic Parameters on Hardness of W6Mo5Cr4V2 High-Speed Steel
摘 要
基于前期采用Ansoft有限元分析软件对自制磁能强化装置进行建模仿真的基础上,通过正交试验的方法系统研究了磁场频率、励磁电压、磁化时间和磁场方向对W6Mo5Cr4V2高速钢硬度的影响规律,得到了最佳的交变磁处理参数,并对最佳参数下处理的高速钢组织进行了观察。结果表明:交变磁处理可使高速钢的硬度提高4.6 HRC;最佳的交变磁处理参数为磁场频率5 Hz,励磁电压30 V,磁化时间60 s,试样被测表面和磁力线在同一个平面上;磁场频率和励磁电压对硬度的影响最大,磁场方向和磁化时间的影响较弱;经最佳参数交变磁处理后,碳化物的分布更加均匀,且尺寸更小,从而使得高速钢的硬度提高。
Abstract
Based on modeling and simulating results of self-made magnetization unit using the finite element analysis software Ansoft, the effects of magnetic field frequency, excitation voltage, magnetization time and magnetic orientation on hardness of W6Mo5Cr4V2 high-speed steel were studied by orthogonal experiment method. The best alternating magnetic parameters were achieved and microstrucute under the best magnetic parameters were observed. The results show that alternating magnetic treatment could enhance the hardness of high-speed steel by 4.6 HRC. The optimal alternating magnetic parameters as followed: magnetic field frequency was 5 Hz, excitation voltage was 30 V, magnetization time was 60 s, measured surface of the sample was on the same plane with the magnetic field line. Magnetic field frequency and excitation voltage had the largest influence on hardness, and magnetic orientation and magnetization time had relative weak influnce. After alternating magnetic treatment with the best parameters, the hardness of high-speed steel increased due to more homogeneous and smaller carbides.
中图分类号 TG156.97 TG711 DOI 10.11973/jxgccl201511012
所属栏目 新材料 新工艺
基金项目 江西省教育厅重点科技项目资助(GJJ11021)
收稿日期 2014/9/10
修改稿日期 2015/6/16
网络出版日期
作者单位点击查看
备注朱涛(1989-),男,湖北荆州人,硕士研究生。
引用该论文: ZHU Tao,LIU Zheng,DENG Ke-yue,SHEN Jun-bo,WU Qiang. Effects of Alternating Magnetic Parameters on Hardness of W6Mo5Cr4V2 High-Speed Steel[J]. Materials for mechancial engineering, 2015, 39(11): 52~55
朱涛,刘政,邓可月,沈俊波,吴强. 交变磁处理参数对W6Mo5Cr4V2高速钢硬度的影响[J]. 机械工程材料, 2015, 39(11): 52~55
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】刘战强,万熠, 周军.高速切削刀具材料及其应用[J]. 机械工程材料,2006,30(5):1-5.
【2】王启民,黄健, 王成勇, 等.高速切削刀具物理气相沉积涂层研究进展[J]. 航空制造技术, 2013(14):78-83.
【3】戴兵,王博, 张恒华, 等. 具有表面类金刚石膜高速钢的耐磨性能[J]. 机械工程材料,2010,34(4):51-54.
【4】景旭文,唐馨如. 提高刀具耐用度的磁处理技术研究[J]. 机械设计与制造,2002(5):81-83.
【5】CAI Z P, ZHAO H Y. Plastic deformation caused by pulsed magnetic treatment of mid-carbon steel [J]. Materials Science and Engineering:A,2007,458(2):262-267.
【6】POLYARUS E N, OLIKER V E. Effect of magnetic field on residual stresses in NiAl-Re detonation coatings [J]. Powder Metallurgy and Metal Ceramics,2011,50(9/10):671-675.
【7】BOCKSTEDT J, KLAMECKI B E. Effects of pulsed magnetic field on thrust bearing washer hardness [J]. Wear,2007,262(9/10): 1086-1096.
【8】LEE C K, LEE W. The effect of magnetic fields for laser welding process using carbon steel [J]. International Journal of Precision Engineering and Manufacturing,2013,14(11):1915-1923.
【9】宋燕利. 低频交变磁场作用下铁磁性材料组织性能变化规律的研究[D].武汉:武汉理工大学,2008:35-36.
【10】李勇, 姜新通, 史庆夫, 等.基于Ansoft的IPM永磁同步电动机磁场计算[J].微特电机,2011(6):1-4.
【11】方萍, 何延. 试验设计与统计[M].杭州:浙江大学出版社, 2003.
【12】SHEN J X, LI P, HAO H, et al. Study on electromagnetic losses in high-speed permanent magnet brushless machines-the state of the art [J]. Proceedings of the CSEE, 2013,33(3):62-74.
【13】CAI Z P, DUAN X J, LIN J, et al. Magnetostriction varieties and stress relief caused by pulsed magnetic field [J]. Journal of Mechanical Engineering,2011,6(3):354-358.
【14】LI Y J, TENG Y F, YANG Y S.Refinement mechanism of low voltage pulsed magnetic field on solidification structure of silicon steel [J]. Metals and Materials International, 2014,20(3):527-530.
【15】蔡志鹏,林健,赵海燕,等. 45#钢在低频间歇磁场作用下晶界移动现象的研究[J]. 清华大学学报(自然科学版),2010,50(7):984-988.
【16】王昕. 脉冲磁化处理提高刀具使用寿命研究[D].大连.大连理工大学,2007:15-16.
【17】林健,赵海燕. 钢铁材料中残余应力与磁致振动的相互作用关系[J].金属学报,2008,44(4):451-456.
【2】王启民,黄健, 王成勇, 等.高速切削刀具物理气相沉积涂层研究进展[J]. 航空制造技术, 2013(14):78-83.
【3】戴兵,王博, 张恒华, 等. 具有表面类金刚石膜高速钢的耐磨性能[J]. 机械工程材料,2010,34(4):51-54.
【4】景旭文,唐馨如. 提高刀具耐用度的磁处理技术研究[J]. 机械设计与制造,2002(5):81-83.
【5】CAI Z P, ZHAO H Y. Plastic deformation caused by pulsed magnetic treatment of mid-carbon steel [J]. Materials Science and Engineering:A,2007,458(2):262-267.
【6】POLYARUS E N, OLIKER V E. Effect of magnetic field on residual stresses in NiAl-Re detonation coatings [J]. Powder Metallurgy and Metal Ceramics,2011,50(9/10):671-675.
【7】BOCKSTEDT J, KLAMECKI B E. Effects of pulsed magnetic field on thrust bearing washer hardness [J]. Wear,2007,262(9/10): 1086-1096.
【8】LEE C K, LEE W. The effect of magnetic fields for laser welding process using carbon steel [J]. International Journal of Precision Engineering and Manufacturing,2013,14(11):1915-1923.
【9】宋燕利. 低频交变磁场作用下铁磁性材料组织性能变化规律的研究[D].武汉:武汉理工大学,2008:35-36.
【10】李勇, 姜新通, 史庆夫, 等.基于Ansoft的IPM永磁同步电动机磁场计算[J].微特电机,2011(6):1-4.
【11】方萍, 何延. 试验设计与统计[M].杭州:浙江大学出版社, 2003.
【12】SHEN J X, LI P, HAO H, et al. Study on electromagnetic losses in high-speed permanent magnet brushless machines-the state of the art [J]. Proceedings of the CSEE, 2013,33(3):62-74.
【13】CAI Z P, DUAN X J, LIN J, et al. Magnetostriction varieties and stress relief caused by pulsed magnetic field [J]. Journal of Mechanical Engineering,2011,6(3):354-358.
【14】LI Y J, TENG Y F, YANG Y S.Refinement mechanism of low voltage pulsed magnetic field on solidification structure of silicon steel [J]. Metals and Materials International, 2014,20(3):527-530.
【15】蔡志鹏,林健,赵海燕,等. 45#钢在低频间歇磁场作用下晶界移动现象的研究[J]. 清华大学学报(自然科学版),2010,50(7):984-988.
【16】王昕. 脉冲磁化处理提高刀具使用寿命研究[D].大连.大连理工大学,2007:15-16.
【17】林健,赵海燕. 钢铁材料中残余应力与磁致振动的相互作用关系[J].金属学报,2008,44(4):451-456.
相关信息