钒改进钢再热裂纹的超声检测方法
Ultrasonic Testing Method for Reheat Crack of Vanadium Modified Steel
摘 要
参考标准API934A对再热裂纹的检测指导意见,设计制作了模拟再热裂纹的对比试块,采用超声衍射时差法（TOFD）、手工脉冲反射式超声法（UT）、磁记忆检测三种方法探索对钒改进钢再热裂纹的检出和标定。结果表明,TOFD+UT组合检测工艺可以实现对模拟再热裂纹（0.4 mm×4 mm×4 mm）的检出和标定,磁记忆检测也可以作为检测再热裂纹的一种补充检测方法。
衍射时差法超声检测
手工脉冲反射超声检测
磁记忆检测
Reheat crack
Time of flight diffraction(TOFD)
Manual pulse-echo shear wave UT
Magnetic memory testing
Abstract
According to the API934A about guidance for inspection for transverse reheat cracking,this paper has designed and fabricated one TOFD sensitivity demonstration block which can simulate reheat crack and explore the detection and quantification of reheat crack by using three inspection methods of TOFD,manual pulse-echo shear wave UT and magnetic memory testing. Testing shows that TOFD+UT combination detection craft can realize the detection and quantitative evaluation for the simulated reheat crack (0.4 mm×4 mm×4 mm) and magnetic memory testing also can be used as one supplementary method of detecting reheat crack.
中图分类号 TG115.28 DOI 10.11973/wsjc201511017
所属栏目 试验研究
基金项目 国家863计划资助项目(2012AA040103)
收稿日期 2015/5/5
修改稿日期
网络出版日期
作者单位点击查看
备注李卫(1991-),男,硕士,主要从事超声衍射时差法检测技术研究。
引用该论文: LI Wei,GUAN Wei-he,CHEN Jian-yu,QI Jie,GUO Peng-jü. Ultrasonic Testing Method for Reheat Crack of Vanadium Modified Steel[J]. Nondestructive Testing, 2015, 37(11): 73～77
李卫,关卫和,陈建玉,齐杰,郭鹏举. 钒改进钢再热裂纹的超声检测方法[J]. 无损检测, 2015, 37(11): 73～77
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】俞树荣. 压力容器设计制造入门与精通［M］.北京：机械工业出版社,2012.
【2】仇恩沧.国产3Cr-1Mo-1/4V钢加氢反应器的开发［J］. 石油化工设备技术,2000(4):36-40.
【3】柳曾典,陈进,卜华全,等. 2.25Cr-1Mo-0.25V钢加氢反应器开发与制造中的一些问题［J］. 压力容器,2011(5):33-40.
【4】CDRIC C,SYLVAIN P. Prevention of weld metal reheat cracking during Cr-Mo-V heavy reactors fabrication［C］∥Proceedings of the ASME 2009 Pressure Vessels and Piping Division Conference PVP2009-78144.Prague:［s.n］,2009.
【5】阎长周,关卫和,陈建玉,等. TOFD方法在厚壁承压设备焊缝检测中的试验和应用［J］. 压力容器,2008(10):7-10.
【6】API Recommended Practice 934-A Materials and fabrication of 2.25Cr-1Mo,2.25Cr-1Mo-0.25V,3Cr-1Mo,and 3Cr-1Mo-0.25V steel heavy wall pressure vessels for high-temperature,high-pressure hydrogen service［S］.
【7】任吉林,林俊明,任文坚,等. 金属磁记忆检测技术研究现状与发展前景［J］. 无损检测,2012,34(4):3-11.
【2】仇恩沧.国产3Cr-1Mo-1/4V钢加氢反应器的开发［J］. 石油化工设备技术,2000(4):36-40.
【3】柳曾典,陈进,卜华全,等. 2.25Cr-1Mo-0.25V钢加氢反应器开发与制造中的一些问题［J］. 压力容器,2011(5):33-40.
【4】CDRIC C,SYLVAIN P. Prevention of weld metal reheat cracking during Cr-Mo-V heavy reactors fabrication［C］∥Proceedings of the ASME 2009 Pressure Vessels and Piping Division Conference PVP2009-78144.Prague:［s.n］,2009.
【5】阎长周,关卫和,陈建玉,等. TOFD方法在厚壁承压设备焊缝检测中的试验和应用［J］. 压力容器,2008(10):7-10.
【6】API Recommended Practice 934-A Materials and fabrication of 2.25Cr-1Mo,2.25Cr-1Mo-0.25V,3Cr-1Mo,and 3Cr-1Mo-0.25V steel heavy wall pressure vessels for high-temperature,high-pressure hydrogen service［S］.
【7】任吉林,林俊明,任文坚,等. 金属磁记忆检测技术研究现状与发展前景［J］. 无损检测,2012,34(4):3-11.
相关信息