Polishing Process and Its Affecting Factors of Chemical Milling for 2197 Al-Li Alloy
摘 要
通过正交试验筛选了适合2197铝锂合金化学铣切加工抛光工艺的槽液配方, 探讨了材料状态、抛光温度和抛光时间对2197铝锂合金碱腐蚀及化学铣切后表面抛光性能的影响。结果表明,HNO3含量和温度是影响抛光效果的主要因素, CrO3的影响次之, HF最小。材料的不同状态对抛光有较大影响, T8态过时效的铝锂合金抛光后粗糙度最小, T6态欠时效的铝锂合金抛光后粗糙度最大。当抛光的配方和工艺条件为硝酸250 g/L、铬酐10 g/L、氢氟酸2 g/L、抛光时间2~3 min、抛光温度25 ℃时, 2197铝锂合金化铣表面能获得良好的抛光效果。
Abstract
The solution formula of polishing process for 2197 Al-Li aluminum alloy was determined by orthogonal experiments, and the major influencing factors of material status, polishing temperature and polishing time were investigated. The results showed that the concentration of HNO3 and temperature were the main factors influencing the polishing effect. The second was CrO3, HF had the minimum influence. Different states of materials had great influence on the polishing, T8 state aging of aluminum lithium alloy had the minimum roughness after polishing, T6 state short aging aluminum lithium alloy had the maximum roughness after polishing. Under the conditions of HHO3 250 g/L, CrO3 10 g/L, HF 2 g/L, polishing temperature 25 ℃ and polishing time 2~3 min, good performance of surface polishing could be obtained.
中图分类号 TG178 TG146.2 DOI 10.11973/fsyfh-201511021
所属栏目 应用技术
基金项目 铝锂合金化铣工艺研究(省教育厅重点实验室项目)
收稿日期 2014/11/3
修改稿日期
网络出版日期
作者单位点击查看
联系人作者刘刚(liugang@126.com)
备注刘刚(1976-), 讲师, 硕士, 从事金属材料腐蚀与防护研究,
引用该论文: LIU Gang,MENG Hai-yan. Polishing Process and Its Affecting Factors of Chemical Milling for 2197 Al-Li Alloy[J]. Corrosion & Protection, 2015, 36(11): 1109
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】易慧芝,邓飞跃,张忠亭. 2197铝锂合金化学铣切工艺研究[J]. 表面技术,2010,39(4): 73-76.
【2】CAKR O. Chemical etching of aluminum[J]. Journal of Materials Processing Technology,2008,199(1/3): 337-340.
【3】CAKR O,TEMEL O,KIYAK H M. Chemical etching of Cu-ETP copper[J]. Journal of Materials Processing Technology,2005(162/163): 275-279.
【4】张钰. 铝锂合金在航天航空中的应用[J]. 铝加工,2009(3): 50-53.
【5】尹茂生,廖广其,蒋洪俊. 铝合金化学铣切常见故障浅析[J]. 涂装与电镀,2008(4): 47-48.
【6】赵永岗,张春刚,王辉,等. 化学铣切在钛合金加工中的研究及应用[J]. 表面技术,2009,38(6): 83-85.
【7】陈祖秋. 我国铝制品化学抛光工艺开发现状[J]. 表面技术,1999(28): 1-2.
【8】陈祖秋. 国内铝制品无黄烟化学抛光工艺的研究现状[J]. 材料保护,1999,32(4): 9-10.
【9】黄兰萍. 2197铝锂合金组织和性能的研究[D]. 长沙: 中南大学,2002.
【10】郭瑞光,李晓杰,唐长斌,等. 铸铝表面绿色环保化学处理新工艺[J]. 电镀与涂饰,2009,29(4): 22-23.
【11】廖广其,尹茂生,朱晓英. 化学铣切对铝合金基体粗糙度的影响[J]. 涂料涂装与电镀,2005,3(6): 38-39.
【12】毛大恒,韩德夫,周亚军,等. 2197铝锂合金的化学铣切工艺的探讨[J]. 材料保护,2010,43(10): 33-35.
【13】HB/Z 5125-2008铝锂合金在碱性溶液中化学铣切工艺[S].
【14】尚佳阳,刘刚,陈玮. 铝锂合金化学铣切液中复合添加剂的研究[J]. 数字化用户,2013,19(13): 116-117.
【15】尹茂生. 钛离子含量对钛合金化学铣切的影响[J]. 涂料涂装与电镀,2006,4(3): 34-35.
【16】刘刚,孟海燕. 2197铝锂合金碱性化铣加工工艺及其影响因素研究[J]. 南昌航空大学学报: 自然科学版,2014,28(3): 64-70.
【17】岳磊磊,张金生,李卫东. 铝合金弱侵蚀镜面化学抛光工艺研究[J]. 武汉纺织大学学报,2014,27(3): 71-73.
【18】张艺,尹自强,尹国举. 铝合金表面的直接光学抛光实验[J]. 应用光学,2014,35(4): 667.
【19】林翠,蔡剑,曾丰光,等. LY12铝锂合金化铣工艺及加工质量影响[J]. 失效分析与预防,2010,5(1): 8-12.
【20】GREGSON P J,FLOWER H M. Microstructural control of toughness in aluminium-lithium alloys[J]. Acta Metall,1985,33(3): 527.
【21】金晓伟. 铝合金状态对化学铣切粗糙度的影响[J]. 涂装与电镀,2010(3): 39-40.
【22】HARRIS S J,NOBLE B,DINSDALE K. The role of magnesium in Al-Li-Mg-Zr alloys[J]. Journal De physique,1987,48(c-3): 415-423.
【2】CAKR O. Chemical etching of aluminum[J]. Journal of Materials Processing Technology,2008,199(1/3): 337-340.
【3】CAKR O,TEMEL O,KIYAK H M. Chemical etching of Cu-ETP copper[J]. Journal of Materials Processing Technology,2005(162/163): 275-279.
【4】张钰. 铝锂合金在航天航空中的应用[J]. 铝加工,2009(3): 50-53.
【5】尹茂生,廖广其,蒋洪俊. 铝合金化学铣切常见故障浅析[J]. 涂装与电镀,2008(4): 47-48.
【6】赵永岗,张春刚,王辉,等. 化学铣切在钛合金加工中的研究及应用[J]. 表面技术,2009,38(6): 83-85.
【7】陈祖秋. 我国铝制品化学抛光工艺开发现状[J]. 表面技术,1999(28): 1-2.
【8】陈祖秋. 国内铝制品无黄烟化学抛光工艺的研究现状[J]. 材料保护,1999,32(4): 9-10.
【9】黄兰萍. 2197铝锂合金组织和性能的研究[D]. 长沙: 中南大学,2002.
【10】郭瑞光,李晓杰,唐长斌,等. 铸铝表面绿色环保化学处理新工艺[J]. 电镀与涂饰,2009,29(4): 22-23.
【11】廖广其,尹茂生,朱晓英. 化学铣切对铝合金基体粗糙度的影响[J]. 涂料涂装与电镀,2005,3(6): 38-39.
【12】毛大恒,韩德夫,周亚军,等. 2197铝锂合金的化学铣切工艺的探讨[J]. 材料保护,2010,43(10): 33-35.
【13】HB/Z 5125-2008铝锂合金在碱性溶液中化学铣切工艺[S].
【14】尚佳阳,刘刚,陈玮. 铝锂合金化学铣切液中复合添加剂的研究[J]. 数字化用户,2013,19(13): 116-117.
【15】尹茂生. 钛离子含量对钛合金化学铣切的影响[J]. 涂料涂装与电镀,2006,4(3): 34-35.
【16】刘刚,孟海燕. 2197铝锂合金碱性化铣加工工艺及其影响因素研究[J]. 南昌航空大学学报: 自然科学版,2014,28(3): 64-70.
【17】岳磊磊,张金生,李卫东. 铝合金弱侵蚀镜面化学抛光工艺研究[J]. 武汉纺织大学学报,2014,27(3): 71-73.
【18】张艺,尹自强,尹国举. 铝合金表面的直接光学抛光实验[J]. 应用光学,2014,35(4): 667.
【19】林翠,蔡剑,曾丰光,等. LY12铝锂合金化铣工艺及加工质量影响[J]. 失效分析与预防,2010,5(1): 8-12.
【20】GREGSON P J,FLOWER H M. Microstructural control of toughness in aluminium-lithium alloys[J]. Acta Metall,1985,33(3): 527.
【21】金晓伟. 铝合金状态对化学铣切粗糙度的影响[J]. 涂装与电镀,2010(3): 39-40.
【22】HARRIS S J,NOBLE B,DINSDALE K. The role of magnesium in Al-Li-Mg-Zr alloys[J]. Journal De physique,1987,48(c-3): 415-423.
相关信息