某电厂轴承弹簧断裂分析
Fracture Analysis on Bearing Spring of One Power Plant
摘 要
某电厂机组的轴承下部弹簧发生断裂，通过对断裂弹簧进行化学成分分析、硬度测试、金相检验及断口分析，研究了轴承弹簧的断裂原因。结果表明: 轴承弹簧断裂的性质为疲劳断裂，弹簧断裂的主要原因是弹簧表面存在原始缺口且服役环境中含有腐蚀性介质。
疲劳断裂
腐蚀
bearing spring
fatigue fracture
corrosion
Abstract
The bearing spring of lower part on a turbine of one power plant had fractured. By means of chemical compositions analysis, hardress test, metallographic inspection and fracture surface analysis, the fracture reasons of the bearing spring were researched. The results show that the fracture mechanism of the bearing spring was fatigue fracture. The fracture failure of the spring was due to original defect of spring surface and corrosive medium in the service environment.
中图分类号 TH135 DOI 10.11973/lhjy-wl201511017
所属栏目 质量控制与失效分析
基金项目
收稿日期 2014/12/8
修改稿日期
网络出版日期
作者单位点击查看
备注李海霞(1987-),女,工程师,硕士。
引用该论文: LI Hai-xia,ZHANG Xiao-wu,WANG Mei-ying,LI Xing-dong. Fracture Analysis on Bearing Spring of One Power Plant[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2015, 51(11): 817～819
李海霞,张小伍,王梅英,李兴东. 某电厂轴承弹簧断裂分析[J]. 理化检验－物理分册, 2015, 51(11): 817～819
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】王永杰.阀门弹簧失效的原因及预防［J］.机械工程师，2011(6):129-130.
【2】任颂赞,张静江,陈质如.钢铁金相图谱［M］.上海:上海科学技术文献出版社,2003.
【3】白云岭.汽车发动机气门弹簧断裂分析［J］.理化检验-物理分册,2013,49(7):476-478.
【4】张栋,钟培道,陶春虎.失效分析［M］.北京:国防工业出版社,2008.
【5】高军,张娜. 脚踏开关弹簧断裂原因分析［J］.金属热处理,2013,38(3):109-111.
【2】任颂赞,张静江,陈质如.钢铁金相图谱［M］.上海:上海科学技术文献出版社,2003.
【3】白云岭.汽车发动机气门弹簧断裂分析［J］.理化检验-物理分册,2013,49(7):476-478.
【4】张栋,钟培道,陶春虎.失效分析［M］.北京:国防工业出版社,2008.
【5】高军,张娜. 脚踏开关弹簧断裂原因分析［J］.金属热处理,2013,38(3):109-111.
相关信息