高酸原油加工用常压塔顶循环回流系统的腐蚀原因
Corrosion Reasons of Overhead Circulation System of Atmospheric Tower for Processing Crude Oil with High Acid Value
摘 要
针对某厂石化常压塔顶循环回流(简称常顶循)系统加工高酸原油过程中出现的腐蚀加重现象, 对常压塔顶循油和塔顶冷凝水中的腐蚀介质进行了分析, 同时利用X射线衍射及X射线能谱分析了常顶循换热器、过滤器釜头侧等部位的腐蚀产物。结果表明:氯化氢、硫化氢是引起常顶循系统腐蚀的主要原因, 高温下环烷酸分解生成二氧化碳、常顶循油具有弱酸性及小分子羧酸的存在也是造成常顶循腐蚀的重要因素。
常压塔
顶循环回流
腐蚀
crude oil with high acid value
atmospheric tower
overhead circulating reflux
corrosion
Abstract
Aiming at a phenomenon that the corrosion of the overhead circulation of atmospheric tower for processing crude oil with high acid value in some petrochemical corporation was aggravated, the corrosion media in top cycle oil and overhead condensed water of atmospheric tower were analyzed. At the same time, the corrosion products in heat exchanger and filter of the overhead circulation of atmospheric tower were analyzed by XRD and EDS. The experimental results indicate that hydrogen chloride and hydrogen sulfide were the main causes of corrosion. The decomposition of naphthenic acid into carbon dioxide at high temperature, the mild acidity of the top cycle oil in atmospheric tower and the existence of small molecular carboxylic acid were the important causes of corrosion.
中图分类号 TE624 DOI 10.11973/fsyfh-201512018
所属栏目 应用技术
基金项目 大学生创新创业训练计划(20131069)
收稿日期 2015/2/6
修改稿日期
网络出版日期
作者单位点击查看
备注项玉芝(1963-), 教授, 博士, 从事石油有机化学及精细化工研究,
引用该论文: XIANG Yu-zhi,ZHANG Lei,WANG Yu-jie,WANG Xue,XIA Dao-hong,LIU Ren-xu,WANG Ji-liang. Corrosion Reasons of Overhead Circulation System of Atmospheric Tower for Processing Crude Oil with High Acid Value[J]. Corrosion & Protection, 2015, 36(12): 1190
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】钱伯章, 朱建芳. 中国炼油工业现状与发展趋势[J]. 天然气与石油, 2009, 27(2): 30-33.
【2】KIM J,LIM W,LEE Y,et al. Development of corrosion control document database system in crude distillation unit[J]. Industrial & Engineering Chemistry Research,2011,50(13):8272-8277.
【3】王玉洁. 加工高酸原油常顶循系统腐蚀原因及缓蚀剂合成与筛选[D]. 青岛: 中国石油大学(华东), 2014: 24,37-41.
【4】陆克平. 等量电位滴定法测定炼油厂高硫污水中氯化物[J]. 石油炼制与化工, 2008,12(39): 55-58.
【5】高鑫. 原油及渣油中铁含量分布分析及脱除研究[D]. 青岛: 中国石油大学(华东),2012:23-24.
【6】董泽华, 何金杯, 郭兴蓬,等. 环烷酸与有机硫对Cr5Mo钢高温腐蚀的交互作用研究[J]. 中国腐蚀与防护学报,2011,6(31): 219-224.
【7】HO T Y,ROGERS M A,DRUSHEL H V,et al. Evolution of sulfur compounds in crude oils[J]. AAPG Bulletin,1974,58(11):2338-2348.
【8】许小云. 加工高硫高酸原油常减压装置防腐要点的探讨[J]. 腐蚀科学与防护技术, 2013, 25(6): 543-546.
【9】关建庆, 王树涛, 黄雪松, 等. 元素硫对抗硫套管钢P110SS腐蚀行为的影响[J]. 腐蚀与防护, 2013, 34(8): 663-666.
【10】SUBRAMANIYAM M,SHAH P. Corrosion control with high-acid crudes[J]. Petroleum technology quarterly,2013,18(4):1-17.
【11】刘良, 缪磊, 汉继程. 加工高酸原油的防腐蚀技术综述[J]. 腐蚀与防护, 2011,32(7): 540-541.
【12】张崇林, 丁明生. 环烷酸对减压塔顶空冷器腐蚀的影响及对策[J]. 石油化工腐蚀与防护, 2012,29(2): 34-37.
【13】陈长风. 油套管钢CO2腐蚀电化学行为与腐蚀产物膜特性研究[D]. 西安: 西北工业大学, 2002:2-5.
【14】何庆龙, 孟惠民, 俞宏英, 等. N80油套管钢CO2腐蚀的研究进展[J]. 中国腐蚀与防护学报, 2007,27(3): 186-192.
【15】OGUNDELE G I,WHITE W E. Some observations on corrosion of carbon steel in aqueous environments containing carbon dioxide[J]. Corrosion, 1986,42(2): 71-78.
【2】KIM J,LIM W,LEE Y,et al. Development of corrosion control document database system in crude distillation unit[J]. Industrial & Engineering Chemistry Research,2011,50(13):8272-8277.
【3】王玉洁. 加工高酸原油常顶循系统腐蚀原因及缓蚀剂合成与筛选[D]. 青岛: 中国石油大学(华东), 2014: 24,37-41.
【4】陆克平. 等量电位滴定法测定炼油厂高硫污水中氯化物[J]. 石油炼制与化工, 2008,12(39): 55-58.
【5】高鑫. 原油及渣油中铁含量分布分析及脱除研究[D]. 青岛: 中国石油大学(华东),2012:23-24.
【6】董泽华, 何金杯, 郭兴蓬,等. 环烷酸与有机硫对Cr5Mo钢高温腐蚀的交互作用研究[J]. 中国腐蚀与防护学报,2011,6(31): 219-224.
【7】HO T Y,ROGERS M A,DRUSHEL H V,et al. Evolution of sulfur compounds in crude oils[J]. AAPG Bulletin,1974,58(11):2338-2348.
【8】许小云. 加工高硫高酸原油常减压装置防腐要点的探讨[J]. 腐蚀科学与防护技术, 2013, 25(6): 543-546.
【9】关建庆, 王树涛, 黄雪松, 等. 元素硫对抗硫套管钢P110SS腐蚀行为的影响[J]. 腐蚀与防护, 2013, 34(8): 663-666.
【10】SUBRAMANIYAM M,SHAH P. Corrosion control with high-acid crudes[J]. Petroleum technology quarterly,2013,18(4):1-17.
【11】刘良, 缪磊, 汉继程. 加工高酸原油的防腐蚀技术综述[J]. 腐蚀与防护, 2011,32(7): 540-541.
【12】张崇林, 丁明生. 环烷酸对减压塔顶空冷器腐蚀的影响及对策[J]. 石油化工腐蚀与防护, 2012,29(2): 34-37.
【13】陈长风. 油套管钢CO2腐蚀电化学行为与腐蚀产物膜特性研究[D]. 西安: 西北工业大学, 2002:2-5.
【14】何庆龙, 孟惠民, 俞宏英, 等. N80油套管钢CO2腐蚀的研究进展[J]. 中国腐蚀与防护学报, 2007,27(3): 186-192.
【15】OGUNDELE G I,WHITE W E. Some observations on corrosion of carbon steel in aqueous environments containing carbon dioxide[J]. Corrosion, 1986,42(2): 71-78.
相关信息