某油田单井管线绝缘接头的腐蚀原因
Corrosion Reason for Insulating Joint in an Oil Field
摘 要
阴极保护系统中, 绝缘接头非阴极保护侧金属管段腐蚀穿孔是绝缘接头的失效情况之一, 新疆某油田出现上述情况。通过对绝缘接头两侧短接显微组织观察、两端电势的测量, 及现场实际工况的分析, 揭示了非保护侧管段腐蚀穿孔的原因, 并提出了合适的防治措施。
阴极保护
腐蚀
insulating joint
cathodic protection
corrosion
Abstract
It′s one of the insulating joint failures that the side without catholic protection was corroded, such a situation happened in Xinjiang. The causes of corrosion perforation on the side of the insulating joint without catholic protection were analyzed by observing the microstructure, measuring the potential between the both side of the insulating joint and analyzing the in-situ situation. Some suitable control measures were put forward.
中图分类号 TG172 DOI 10.11973/fsyfh-201512021
所属栏目 失效分析
基金项目
收稿日期 2014/12/22
修改稿日期
网络出版日期
作者单位点击查看
备注陈博(1987-),工程师,本科,从事油气田腐蚀与防护工作,
引用该论文: PENG Bo,CHEN Bo,CHEN Ji-wang,YAO Peng-cheng,DU Jin-nan. Corrosion Reason for Insulating Joint in an Oil Field[J]. Corrosion & Protection, 2015, 36(12): 1202
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】赵发银, 吴万兴. 不锈钢结构件防腐及表面处理技术[J]. 兵工自动化,2009,10:18-20.
【2】SY/T 0086-2003 阴极保护管道的电绝缘标准[S].
【3】胡士信. 阴极保护工程[M]. 北京: 化学工业出版社, 1999.
【4】GB/T 21246-2007 埋地钢质管道阴极保护参数测量方法[S].
【5】SY/T 0516-2008 绝缘接头与绝缘法兰技术规范[S].
【6】曹楚南. 腐蚀电化学原理[M]. 北京: 化学工业出版社,2008:36.
【7】胡建华. 石油库金属油管的安全监测[J]. 石油库与加油站,2009(3):78-79.
【2】SY/T 0086-2003 阴极保护管道的电绝缘标准[S].
【3】胡士信. 阴极保护工程[M]. 北京: 化学工业出版社, 1999.
【4】GB/T 21246-2007 埋地钢质管道阴极保护参数测量方法[S].
【5】SY/T 0516-2008 绝缘接头与绝缘法兰技术规范[S].
【6】曹楚南. 腐蚀电化学原理[M]. 北京: 化学工业出版社,2008:36.
【7】胡建华. 石油库金属油管的安全监测[J]. 石油库与加油站,2009(3):78-79.
相关信息