捞渣机链条断裂原因分析
Fracture Reasons Analysis on the Chain of Submerged Chain Conveyor
摘 要
通过化学成分分析、抗拉强度测试、表面硬度测试、断口分析、金相检验的方法,对捞渣机链条的断裂原因进行了分析。结果表明: 链条断裂的主要原因是焊接部位在渗碳淬火后沿晶界产生了裂纹，该沿晶裂纹降低了链条的承载能力和使用寿命，导致链条仅使用了一个多月即发生断裂。
链条
断裂
沿晶裂纹
submerged chain conveyor
chain
fracture
intergranular crack
Abstract
Fracture Reasons of the chain of submerged chain conveyor were analyzed by chemical composition analysis, tensile strength test, surface hardness test, fracture surface analysis, and metallographic analysis. The results show that the fracture of the chain was caused by intergranular cracks at the welding position after carburizing and quenching. The intergranular cracks decreased the carrying capacity and the working life of the chain, resulting in the fracture after use for more than one month.
中图分类号 TG115.2 DOI 10.11973/lhjy-wl201601019
所属栏目 质量控制与失效分析
基金项目
收稿日期 2015/9/11
修改稿日期
网络出版日期
作者单位点击查看
备注王伟旬(1980-),男,工程师,学士.
引用该论文: WANG Wei-xun,GUAN Gui-fen. Fracture Reasons Analysis on the Chain of Submerged Chain Conveyor[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2016, 52(1): 71～73
王伟旬,关桂芬. 捞渣机链条断裂原因分析[J]. 理化检验－物理分册, 2016, 52(1): 71～73
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】李晓华,杨红曦,张立胜.600 MW锅炉捞渣机链条系统的安装、使用与维护［J］.华电技术,2011,33(7): 41-44.
【2】胡金明.提高煤气化装置捞渣机链条使用寿命的方法研究［J］.湖南农机(学术版),2013(9): 70-71.
【3】侯增寿,范东黎.热处理手册: 第1卷 工艺基础［M］.3版.北京: 机械工业出版社,2001: 101.
【4】刘永飞,王平怀,党恩,等.20CrNiMo钢零件渗碳表层淬火开裂原因分析［J］.理化检验-物理分册,2014,50(3): 229-231.
【5】姚亚俊,罗长增,石巨岩,等.17CrNiMo6钢大型重载内齿圈渗碳淬火畸变控制［J］.金属热处理,2014,39(1): 137-140.
【6】王金海,樊纪新.2 209 t/h锅炉捞渣机链条断裂原因分析及预防措施［J］.热力发电,2005,34(1): 59.
【2】胡金明.提高煤气化装置捞渣机链条使用寿命的方法研究［J］.湖南农机(学术版),2013(9): 70-71.
【3】侯增寿,范东黎.热处理手册: 第1卷 工艺基础［M］.3版.北京: 机械工业出版社,2001: 101.
【4】刘永飞,王平怀,党恩,等.20CrNiMo钢零件渗碳表层淬火开裂原因分析［J］.理化检验-物理分册,2014,50(3): 229-231.
【5】姚亚俊,罗长增,石巨岩,等.17CrNiMo6钢大型重载内齿圈渗碳淬火畸变控制［J］.金属热处理,2014,39(1): 137-140.
【6】王金海,樊纪新.2 209 t/h锅炉捞渣机链条断裂原因分析及预防措施［J］.热力发电,2005,34(1): 59.
相关信息