2Cr13不锈钢止血钳断裂原因分析
Causes Analysis on Fracture of 2Cr13 Stainless Steel Hemostatic Forceps
摘 要
某2Cr13钢有齿止血钳在使用11个月后于刃部发生断裂。采用宏观检验、化学成分分析、硬度测试、金相检验的方法,对止血钳发生断裂的原因进行了分析。结果表明: 由于淬火温度过高，导致止血钳出现淬火裂纹和粗大组织，且淬火后磨削又出现了磨削裂纹，裂纹扩展最终导致失效，最后针对此原因提出了改进措施。
止血钳
断裂
淬火温度
淬火裂纹
磨削裂纹
2Cr13 stainless steel
hemostatic forcep
fracture
quenching temperature
quenching crack
grinding crack
Abstract
The blade of one hemostatic forcep of 2Cr13 stainless steel fractured after being used for 11 months. Macroscopic examination, chemical compositions analysis, hardness testing and metallographic examination were adopted to analyze the fracture reasons of the hemostatic forcep. The results show that due to the too high quenching temperature, quenching cracks and bulky structure generated. Grinding cracks also appeared after quenching and grinding process. The cracks expanded and finally resulted in the fracture. The improvement measures were made according to the fracture reasons of the hemostatic forcep.
中图分类号 TG115.2 DOI 10.11973/lhjy-wl201601020
所属栏目 质量控制与失效分析
基金项目
收稿日期 2015/4/10
修改稿日期
网络出版日期
作者单位点击查看
备注王燕慧(1989-)，女，助理工程师。
引用该论文: WANG Yan-hui,CHEN Zhuo-yue,WANG Li-ping,XU Li-bin,WANG Miao,GUO Jia-qi. Causes Analysis on Fracture of 2Cr13 Stainless Steel Hemostatic Forceps[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2016, 52(1): 74～76
王燕慧,陈卓玥,王丽萍,许李彬,王妙,郭佳琦. 2Cr13不锈钢止血钳断裂原因分析[J]. 理化检验－物理分册, 2016, 52(1): 74～76
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】张平,周上祺.热处理工艺对Cr13型不锈钢组织和性能的影响［J］.特钢技术,2007,13(3): 12-17.
【2】GB/T 1220—2007 不锈钢棒［S］.
【3】GB/T 2766—2006 穿鳃式止血钳通用技术条件［S］.
【4】GB/T 6394-2002 金属平均晶粒度测定法［S］.
【5】陈渝.汽车变速器输入轴校直断裂失效分析［J］.理化检验-物理分册,2014,50(12): 922-925.
【6】岳苗,李锁才,张琴,等.某2Cr13钢零部件裂纹产生原因分析［J］.理化检验-物理分册,2013,49(5): 324-326.
【2】GB/T 1220—2007 不锈钢棒［S］.
【3】GB/T 2766—2006 穿鳃式止血钳通用技术条件［S］.
【4】GB/T 6394-2002 金属平均晶粒度测定法［S］.
【5】陈渝.汽车变速器输入轴校直断裂失效分析［J］.理化检验-物理分册,2014,50(12): 922-925.
【6】岳苗,李锁才,张琴,等.某2Cr13钢零部件裂纹产生原因分析［J］.理化检验-物理分册,2013,49(5): 324-326.
相关信息