固溶碳原子对IF钢Snoek内耗峰的影响
Influence of Solid Solution Carbon Atoms on Snoek Internal Friction Peak of IF Steels
摘 要
为了研究钢中固溶碳原子含量对Snoek内耗峰的影响, 以超低碳汽车板IF钢为研究对象, 通过不同温度的热处理获得不同固溶碳原子含量的试样, 分别进行内耗试验, 并对得出的内耗曲线进行比对分析。结果表明:经过热处理的试样都会产生明显的Snoek内耗峰, 随着固溶碳原子含量的增加, 内耗峰峰高逐渐增加, 而峰温基本保持在325 K左右。
固溶碳原子
内耗
Snoek峰
IF steel
solid solution carbon atom
internal friction
Snoek peak
Abstract
In order to study the influence of solid solution carbon atom contents on Snoek internal friction peak, tests of internal friction were carried out on interstitial free steels with different contents of solid solution carbon atoms obtained by different heat treatment, and the internal friction curves were compared and analyzed. The results show that the Snoek internal friction peak appeared on every sample after heat treatment. The internal friction peak increased with the increase of contents of solid solution carbon atoms while the temperature of the peak remained at about 325 K.
中图分类号 TG161 DOI 10.11973/lhjy-wl201603002
所属栏目
基金项目 上海检验检疫局科技计划资助项目(HK023-2014)
收稿日期 2015/11/8
修改稿日期
网络出版日期
作者单位点击查看
备注徐凌云(1982-),男,高级工程师,工学硕士。
引用该论文: XU Ling-yun,JI Jing,HUANG Jing,ZHU Zi-heng,WU Yi-wen,WANG Hong-bin. Influence of Solid Solution Carbon Atoms on Snoek Internal Friction Peak of IF Steels[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2016, 52(3): 156～158
徐凌云,吉静,黄菁,朱子恒,吴益文,汪宏斌. 固溶碳原子对IF钢Snoek内耗峰的影响[J]. 理化检验－物理分册, 2016, 52(3): 156～158
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】李贺杰,赵劲松,韩静涛,等.IF钢(无间隙原子钢)的发展、应用及展望[J].唐山学院学报,2008,21(4): 3-6.
【2】郑国伟.240 MPa级高强度IF钢的冷轧压下率和退火温度[J].理化检验-物理分册,2014,50(3): 165-168.
【3】吉静,吴益文,徐凌云,等.冷加工变形对IF钢位错密度的影响[J].理化检验-物理分册,2015,51(3): 170-172.
【4】赵辉,王先进.无间隙原子钢的生产与发展[J].钢铁研究,1993(1): 49-54.
【5】王先平,胡菁,庄重,等.自由衰减曲线的全谱拟合及其在高精度内耗测量中的应用[J].理化检验-物理分册,2011,47(7): 399-402.
【6】KE T S. Experimental evidence of the viscous behavior of grain boundaries in metals[J]. Physical Review,1947,71(8): 533-546.
【7】戢景文,车韵怡,刘爱生.钢铁中稀土合金化的内耗研究及其理论[J].中国稀土学报,1996,14(4): 350-358.
【8】戢景文.钢铁中稀土合金化的内耗研究[J].物理,1993,22(4): 208-211.
【9】戢景文,刘芬娣,王登京.汽车钢烘烤硬化性机理的内耗研究[J].金属学报,1999,35(9): 913-919.
【10】金晓龙.预变形和烘烤时间对低碳钢烘烤硬化性能影响的内耗研究[D].鞍山:辽宁科技大学,2013.
【11】RUIZ D, RIVERA-TOVAR J L. Aging phenomena in high-Si steels studied by internal friction[J]. Materials Science and Engineering A, 2006, 442(1): 462-465.
【12】BHADESHIA H, HONEYCOMBE R. Steels: Microstructure and properties[M]. First edition. Cambridge: Hodder Arnold, 1981: 5.
【2】郑国伟.240 MPa级高强度IF钢的冷轧压下率和退火温度[J].理化检验-物理分册,2014,50(3): 165-168.
【3】吉静,吴益文,徐凌云,等.冷加工变形对IF钢位错密度的影响[J].理化检验-物理分册,2015,51(3): 170-172.
【4】赵辉,王先进.无间隙原子钢的生产与发展[J].钢铁研究,1993(1): 49-54.
【5】王先平,胡菁,庄重,等.自由衰减曲线的全谱拟合及其在高精度内耗测量中的应用[J].理化检验-物理分册,2011,47(7): 399-402.
【6】KE T S. Experimental evidence of the viscous behavior of grain boundaries in metals[J]. Physical Review,1947,71(8): 533-546.
【7】戢景文,车韵怡,刘爱生.钢铁中稀土合金化的内耗研究及其理论[J].中国稀土学报,1996,14(4): 350-358.
【8】戢景文.钢铁中稀土合金化的内耗研究[J].物理,1993,22(4): 208-211.
【9】戢景文,刘芬娣,王登京.汽车钢烘烤硬化性机理的内耗研究[J].金属学报,1999,35(9): 913-919.
【10】金晓龙.预变形和烘烤时间对低碳钢烘烤硬化性能影响的内耗研究[D].鞍山:辽宁科技大学,2013.
【11】RUIZ D, RIVERA-TOVAR J L. Aging phenomena in high-Si steels studied by internal friction[J]. Materials Science and Engineering A, 2006, 442(1): 462-465.
【12】BHADESHIA H, HONEYCOMBE R. Steels: Microstructure and properties[M]. First edition. Cambridge: Hodder Arnold, 1981: 5.
相关信息