45钢原始奥氏体晶界的显示方法
A Method to Display the Original Austenite Grain Boundary of 45 Steel
摘 要
利用控温水浴锅, 对经不同工艺热处理的45钢原始奥氏体晶界的显示方法进行了系统的研究。结果表明: 对860 ℃保温1 h水淬的45钢试样进行250 ℃回火15 min 后, 再在70 ℃水浴锅中用30 mL过饱和苦味酸+5 mL缓蚀剂侵蚀10 min, 可清晰地显示出其原始奥氏体晶界。
晶界
45钢
显示方法
original austenite
grain boundary
45 steel
displaying method
Abstract
Using a water bath pot of controlled temperature, the method was systematically studied to display the original austenite grain boundary of 45 steel after different heat-treatment process. The results show that the austenite grain boundaries of 45 steel specimens after tempering heat-treatment at 250 ℃ for 15 min, which were etched by 30 mL supersaturated picric acid and 5 mL corrosion inhibitor in the water bath pot at 70 ℃ for 10 min, could be revealed clearly.
中图分类号 TG115.2 DOI 10.11973/lhjy-wl201603006
所属栏目
基金项目
收稿日期 2015/9/10
修改稿日期
网络出版日期
作者单位点击查看
备注万长杰(1964-), 男, 高级工程师, 学士。
引用该论文: WAN Chang-jie,BAI Rui-juan,SHEN Li-juan,WANG Qing-bo,ZHAO Xin-wei. A Method to Display the Original Austenite Grain Boundary of 45 Steel[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2016, 52(3): 174～176
万长杰,白瑞娟,申丽娟,王清波,赵新伟. 45钢原始奥氏体晶界的显示方法[J]. 理化检验－物理分册, 2016, 52(3): 174～176
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】张海旺, 李朝辉, 汪鹏.45圆钢冷拔加工开裂原因分析[J].理化检验-物理分册, 2015,51(5): 368-369.
【2】万长杰, 白瑞娟, 张胜利, 等.20CrMnTi 齿轮钢铸坯缺陷引起的开裂分析[J].理化检验-物理分册, 2013,49(8): 549-550.
【3】樊东黎.金相腐蚀剂介绍[J].金属热处理, 2008,33(2): 110-111.
【4】王存宇, 付瑞东.一种显示铬钼钒钢奥氏体晶界的方法[J].理化检验-物理分册, 2005,41(5): 265-270.
【5】杨湄, 胡志华.一种显示淬火钢奥氏体晶界的方法[J].四川工业学院学报, 2002,21(1): 65-67.
【6】孙振岩, 刘春明.合金扩散与相变[M].沈阳: 东北大学出版社, 2002:49-52.
【2】万长杰, 白瑞娟, 张胜利, 等.20CrMnTi 齿轮钢铸坯缺陷引起的开裂分析[J].理化检验-物理分册, 2013,49(8): 549-550.
【3】樊东黎.金相腐蚀剂介绍[J].金属热处理, 2008,33(2): 110-111.
【4】王存宇, 付瑞东.一种显示铬钼钒钢奥氏体晶界的方法[J].理化检验-物理分册, 2005,41(5): 265-270.
【5】杨湄, 胡志华.一种显示淬火钢奥氏体晶界的方法[J].四川工业学院学报, 2002,21(1): 65-67.
【6】孙振岩, 刘春明.合金扩散与相变[M].沈阳: 东北大学出版社, 2002:49-52.
相关信息