海南电网变电站金属架构防护涂层的使用情况
Service Conditions of Protective Coatings of Grid Substations in Hainan Province
摘 要
对海南省17个城区33所变电站内设施腐蚀的情况进行了现场考察，调研在海南高温、高湿、高盐条件下，变电站设施金属腐蚀及防护涂层失效的原因,并归纳了现有涂层存在的缺陷,以期为研究适合海南环境中的新型防腐蚀涂料提供依据。结果表明:不同气候环境中变电站设施腐蚀程度不同，现用防腐蚀涂层的腐蚀类型有全面腐蚀和局部腐蚀。
变电站
钢架构
腐蚀
特殊环境
power coating failure
grid substation
steel structure
corrosion
special environment
Abstract
The corrosion phenomena of 33 substation facilities within 17 cities in Hainan province were analyzed, the failure reasons of coatings and metals in substations in high temperature, high humidity and high salt conditions in Hainan were investigated, and the problems existing in the coatings were summarized. It is found that the levels of corrosion were different in different substations. The corrosion types of the coatings include general corrosion and localized corrosion. The purpose of this research was to provide a basis for the study of new anti-corrosion coatings in Hainan environments.
中图分类号 TG172 DOI 10.11973/fsyfh-201603014
所属栏目 应用技术
基金项目 中国南方电网公司科技项目(K-HN2013-001)
收稿日期 2015/3/24
修改稿日期
网络出版日期
作者单位点击查看
联系人作者刘福春(fcliu@imr.ac.cn)
备注刘福春(1966-)，研究员，博士,从事纳米复合涂料和防腐蚀涂层,
引用该论文: YANG Da-ning,ZHAO Shu-yan,FU Chuan-fu,LIU Fu-chun,CHEN Lin-cong,HAN En-hou. Service Conditions of Protective Coatings of Grid Substations in Hainan Province[J]. Corrosion & Protection, 2016, 37(3): 249
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】王昊昊,李碧君,徐泰山,等. 互联电网应对极端外部灾害的调度防御技术的评述[J]. 华东电力,2012,40(1):35-40.
【2】王振尧,陈鸿川,于国才. 海南省的大气腐蚀性调查[J]. 中国腐蚀与防护学报,1996,16(3):225-229.
【3】李天富. 海南岛酸雨分析研究[J]. 广东气象,2002,(3):14-17.
【4】孙心利,高剑峰,董暖. 220 kV变电站金属材料腐蚀原因分析[J]. 河北电力技术,2009,28(4):1-2,34.
【5】石鑫跃,陈颖敏,孙心利. 220 kV变电站铜材腐蚀原因分析与对策[J]. 全面腐蚀控制,2011,12(25):16-18.
【6】高赞,董庆友,张广平,等. 甘肃变电钢构架腐蚀类型调查与分析[J]. 腐蚀科学与防护技术,2014,26(1):95-98.
【7】刘勇,李风雷,刘建秋. 变电站户外钢构支架的腐蚀和防护研究[J]. 工业建筑,2012(42):249-251.
【8】陈云,强春媚,王国刚,等. 输电铁塔的腐蚀与防护[J]. 电力建设,2010,33(8):55-58.
【9】EMAD S I. Corrosion control in electric power systems[J]. Electric Power Systems Research,1999,52(1):9-17.
【10】默增禄,程志云. 输电线路杆塔的腐蚀与防治对策[J]. 电力建设,2004,25(1):22-23.
【11】张成涛,刘宗林,唐小辉. 输配电铁塔的腐蚀与防护[J]. 全面腐蚀控制,1998,12(3):11-15.
【12】王平,孙心利,马东伟,等. 输变电设备大气腐蚀情况调查与分析[J]. 腐蚀科学与防护技术,2012,24(6):525-526.
【13】陈军君,李明,王军,等. 变电站金属构件的常见腐蚀形式及解决措施[J]. 内蒙古电力技术,2013,31(1):7-11.
【14】ALBRECHT P,HALL J T T. Atmospheric corrosion resistance of structural steels[J]. Journal of Materials in Civil Engineering,2003(15):2-24.
【15】梁佶,林书明. 钢结构的大气腐蚀模型[J]. 空间结构,2004,10(4):60-63.
【16】梁彩凤,侯文泰. 环境因素对钢的大气腐蚀的影响[J]. 中国腐蚀与防护学报,1998,18(1):1-6.
【17】胡骞. 缝隙腐蚀的电化学噪声特征及机理研究[D]. 武汉:华中科技大学,2011.
【18】陈东旭,吴欣强,韩恩厚. 缝隙腐蚀研究进展及核电材料的缝隙腐蚀问题[J]. 中国腐蚀与防护学报,2014,34(4):295-299.
【19】SHU H K,FAQEER F M,PICKERING H W. Pitting on the crevice wall prior to crevice corrosion[J]. Electrochimica Acta,2011(56):1719-1728.
【20】KENNELL G F,EVITTS R W,HEPPNER K L. A critical crevice solution and IR drop crevice corrosion model[J]. Corrosion Science,2008(50):1716-1725.
【21】FORCE B D,PICKERING H W. A clearer view of how crevice corrosion occurs[J]. Journal Minerals Metals and Materials Society,1995(47):22-27.
【22】黄安国,王永生,李志远,等. 针状铁素体焊缝金属腐蚀行为的研究[J]. 材料保护,1999,35(10):6-8.
【23】黄安国,李志远,余圣甫,等. 低合金钢焊缝金属的腐蚀行为[J]. 焊接学报,2005,26(11):31-34.
【24】赖春晓. 焊缝腐蚀的原因和解决方法[J]. 全面腐蚀控制,2004,18(6):10.
【2】王振尧,陈鸿川,于国才. 海南省的大气腐蚀性调查[J]. 中国腐蚀与防护学报,1996,16(3):225-229.
【3】李天富. 海南岛酸雨分析研究[J]. 广东气象,2002,(3):14-17.
【4】孙心利,高剑峰,董暖. 220 kV变电站金属材料腐蚀原因分析[J]. 河北电力技术,2009,28(4):1-2,34.
【5】石鑫跃,陈颖敏,孙心利. 220 kV变电站铜材腐蚀原因分析与对策[J]. 全面腐蚀控制,2011,12(25):16-18.
【6】高赞,董庆友,张广平,等. 甘肃变电钢构架腐蚀类型调查与分析[J]. 腐蚀科学与防护技术,2014,26(1):95-98.
【7】刘勇,李风雷,刘建秋. 变电站户外钢构支架的腐蚀和防护研究[J]. 工业建筑,2012(42):249-251.
【8】陈云,强春媚,王国刚,等. 输电铁塔的腐蚀与防护[J]. 电力建设,2010,33(8):55-58.
【9】EMAD S I. Corrosion control in electric power systems[J]. Electric Power Systems Research,1999,52(1):9-17.
【10】默增禄,程志云. 输电线路杆塔的腐蚀与防治对策[J]. 电力建设,2004,25(1):22-23.
【11】张成涛,刘宗林,唐小辉. 输配电铁塔的腐蚀与防护[J]. 全面腐蚀控制,1998,12(3):11-15.
【12】王平,孙心利,马东伟,等. 输变电设备大气腐蚀情况调查与分析[J]. 腐蚀科学与防护技术,2012,24(6):525-526.
【13】陈军君,李明,王军,等. 变电站金属构件的常见腐蚀形式及解决措施[J]. 内蒙古电力技术,2013,31(1):7-11.
【14】ALBRECHT P,HALL J T T. Atmospheric corrosion resistance of structural steels[J]. Journal of Materials in Civil Engineering,2003(15):2-24.
【15】梁佶,林书明. 钢结构的大气腐蚀模型[J]. 空间结构,2004,10(4):60-63.
【16】梁彩凤,侯文泰. 环境因素对钢的大气腐蚀的影响[J]. 中国腐蚀与防护学报,1998,18(1):1-6.
【17】胡骞. 缝隙腐蚀的电化学噪声特征及机理研究[D]. 武汉:华中科技大学,2011.
【18】陈东旭,吴欣强,韩恩厚. 缝隙腐蚀研究进展及核电材料的缝隙腐蚀问题[J]. 中国腐蚀与防护学报,2014,34(4):295-299.
【19】SHU H K,FAQEER F M,PICKERING H W. Pitting on the crevice wall prior to crevice corrosion[J]. Electrochimica Acta,2011(56):1719-1728.
【20】KENNELL G F,EVITTS R W,HEPPNER K L. A critical crevice solution and IR drop crevice corrosion model[J]. Corrosion Science,2008(50):1716-1725.
【21】FORCE B D,PICKERING H W. A clearer view of how crevice corrosion occurs[J]. Journal Minerals Metals and Materials Society,1995(47):22-27.
【22】黄安国,王永生,李志远,等. 针状铁素体焊缝金属腐蚀行为的研究[J]. 材料保护,1999,35(10):6-8.
【23】黄安国,李志远,余圣甫,等. 低合金钢焊缝金属的腐蚀行为[J]. 焊接学报,2005,26(11):31-34.
【24】赖春晓. 焊缝腐蚀的原因和解决方法[J]. 全面腐蚀控制,2004,18(6):10.
相关信息