Fracture Analysis of Butterfly Valve Clack for Nuclear Power Plant
摘 要
利用直读光谱仪、光学显微镜、布氏硬度计、扫描电子显微镜等对某核电站蝶阀阀瓣断裂原因进行了分析。结果表明: 该蝶阀阀瓣的失效模式为沿晶腐蚀断裂, 造成阀瓣断裂的主要原因是其化学成分不符合JIS G 4303-2005的指标要求, 且铸造后未经合适的固溶处理; 阀瓣中晶界上有连续碳化物析出, 存在敏化问题, 在含有腐蚀性元素硫和氯的海水介质中长时间服役后自外向内沿奥氏体晶界发生了沿晶腐蚀断裂。
Abstract
The fracture reason of the butterfly valve clack used in the nuclear power plant was analyzed by means of optical emission spectrometer, optical microscope, Brinell hardness tester and scanning electron microscope (SEM). The results show that the failure mode of the butterfly valve clack was intergranular corrosion fracture. The chemical composition of the valve clack didn′t meet the specified requirement of JIS G 4303-2005 and the solution treatment was inappropriate after casting, which were the main reasons of the valve clack fracture. Continuous carbide was precipitated at the grain boundaries of the valve clack and the grain boundaries were sensitized, resulting in the intergranular corrosion fracture along the austenite grain boundaries after long service in the sea containing corrosive elements of S and Cl.
中图分类号 TG142 DOI 10.11973/jxgccl201604024
所属栏目 失效分析
基金项目
收稿日期 2015/6/1
修改稿日期 2016/2/22
网络出版日期
作者单位点击查看
备注边春华(1982-), 男, 吉林延边人, 工程师, 学士。
引用该论文: BIAN Chun-hua,ZHANG Wei,WANG Yun-wei. Fracture Analysis of Butterfly Valve Clack for Nuclear Power Plant[J]. Materials for mechancial engineering, 2016, 40(4): 107~110
边春华,张维,王云伟. 核电站蝶阀阀瓣断裂原因分析[J]. 机械工程材料, 2016, 40(4): 107~110
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】吴民达, 赵源.机械工程材料测试手册: 腐蚀与摩擦学卷[M].沈阳: 辽宁科学技术出版社, 2002: 156-157.
【2】戴起勋.金属材料学[M].北京: 化学工业出版社, 2005.
【3】张胜寒, 边娜, 史艳玲.奥氏体不锈钢晶间腐蚀研究状况[J], 江苏化工, 2008, 36(3): 45-47.
【2】戴起勋.金属材料学[M].北京: 化学工业出版社, 2005.
【3】张胜寒, 边娜, 史艳玲.奥氏体不锈钢晶间腐蚀研究状况[J], 江苏化工, 2008, 36(3): 45-47.
相关信息